View Patent ↗Photoconductors are disclosed having an overcoat layer of silsesquioxane substituted with 4-[3-(triethoxysilylpropoxy]-2-hydroxybenzophenone. The degree of substitution is believed not critical. Similarly, the thickness of the coating is not critical and may vary according to the wear anticipated, as well as the electrical requirements of the specific application. Improvements are realized using this material in comparison to unsubstituted silsesquioxane.
1. A photoconductor overcoated with a silsesquioxane substituted with a hydrolyzed benzophenone having the following general formula:
where R′ is hydrogen C 1 -C 8 alkyl or halogen, R′″ and R″″ are hydrogen, C 1 -C 8 alkoxy, carboxy, halogen, hydrogen, amino, carbethoxy, or -Q- (CH 2 ) 3 Si(OR″) 3 ; Q is —NH—or —O—; R″ is C 1 -C 8 alkyl; and a is an integer equal to 1-3 inclusive.
2. The overcoated photoconductor of claim 1 in which said hydrolyzed benzophenone substitutes said silsesquioxane in amount of about one said benzophenone-containing group for every 4 to 10 methyl substituted silicon groups.
3. The overcoated photoconductor of claim 1 in which said overcoat is between 0.1 and 5 microns thick.
4. The overcoated photoconductor of claim 1 in which said overcoat is between 0.5 and 2 microns thick.
5. The overcoated photoconductor of claim 1 in which said overcoat is about 0.75 microns thick.
6. A photoconductor overcoated with a silsesquioxane substituted with hydrolyzed 4-[3-triethoxysilylpropoxy]-2-hydroxybenzophenone (SHBP).
7. The overcoated photoconductor of claim 6 wherein said SHBP substitutes said silsesquioxane in amount of about one said SHBP molecule for every 4 to 10 methyl substituted silicon groups.
8. The overcoated photoconductor of claim 7 in which said overcoat is between 0.5 and 2 microns thick.
9. The overcoated photoconductor of claim 7 in which said overcoat is between 0.1 and 5 microns thick.
10. The overcoated photoconductor of claim 7 in which said overcoat is about 0.75 microns thick.
11. The overcoated photoconductor of claim 6 in which said overcoat is between 0.1 and 5 microns thick.
12. The overcoated photoconductor of claim 6 in which said overcoat is between 0.5 and 2 microns thick.
13. The overcoated photoconductor of claim 6 in which said overcoat is about 0.75 microns thick.