Efflorescence control with wax
View Patent ↗A method for making a concrete shaped product more resistant to efflorescence, including forming a mixture of a wax blend with a concrete mix into a shaped product, the wax blend including a weight ratio of 50.01% to 99.99% of a main wax and 0.01% to 49.99% of a secondary wax.
1. A method for making a concrete shaped product more resistant to efflorescence, comprising:
forming a mixture of a wax blend with a concrete mix, said wax blend comprising about 0.25–2.50% inclusive of a total weight of said mixture, said wax blend having a weight ratio of from about 1:1 to 10:1 of a main wax and 0.01 to a secondary wax, said main wax comprising paraffin wax and said secondary wax comprising montan wax, and forming said mixture of the wax blend and the concrete mix into a concrete shaped product, wherein the wax blend makes said concrete shaped product more resistant to efflorescence.
2. The method according to claim 1 , comprising manufacturing the concrete shaped product using a base mix and a face mix, and adding said wax blend substantially just to the face mix alone.
3. The method according to claim 1 , wherein said wax blend comprises at least one of: a wax emulsion of said main wax and said secondary wax and at least one emulsifier, a wax suspension that includes said main wax and said secondary wax suspended in a fluid, and a wax solution that includes said main wax and said secondary wax dissolved in a solvent.
4. The method according to claim 1 , wherein the wax blend has a congealing point 5–15° C. above ambient temperature.
5. The method according to claim 1 , wherein the wax blend has a congealing point at least 10° C. below an autoclave temperature.
6. A method for making a concrete shaped product more resistant to efflorescence, comprising:
partially filling a mold with a concrete base mix and placing a concrete face mix over said concrete base mix, wherein a wax blend is added substantially just to the concrete face mix alone, and curing said concrete base mix and said concrete face mix to form a concrete shaped product, wherein said wax blend in said concrete face mix makes said concrete shaped product more resistant to efflorescence.
7. A concrete shaped product comprising a wax blend mixed with a concrete mix that has been formed into a shaped product, said wax blend comprising about 0.25–2.50% inclusive of a total weight of said mixture, said wax blend having a weight ratio of about 1:1 to 10:1 of a main wax and 0.01 to a secondary wax, said main wax comprising paraffin wax and said secondary wax comprising montan wax.