Elastic nonwoven sheet
View Patent ↗This invention relates to stretchable nonwoven sheets prepared by substantially uniformly impregnating a necked nonwoven substrate or an easily extensible as-made nonwoven substrate with an elastomeric polymer by treatment with an elastomeric polymer solution. The nonwoven sheet is useful in the manufacture of diapers and other hygiene articles.
1. A stretchable nonwoven sheet consisting of a necked nonwoven substrate substantially uniformly impregnated with an elastomeric polymer solution without forming an elastomeric polymer layer on either surface of said substrate, the stretchable nonwoven sheet having a ratio of third unload cycle force at 100% elongation to third load cycle force at 100% elongation, after the stretchable nonwoven sheet has been extended to 140% in the necked direction three times, of at least 0.3:1, wherein the necked nonwoven substrate has a percent elongation in a cross-direction of between about 30% and about 300% and, wherein the stretchable nonwoven sheet has a thickness of 0.25 mm to 0.75 mm.
2. The stretchable nonwoven sheet according to claim 1 wherein the ratio of unload force to load force is at least 0.45:1.
3. The stretchable nonwoven sheet according to claim 1 wherein the sheet comprises about 10-80 weight percent of the elastomeric polymer based on the total weight of elastomeric polymer and nonwoven substrate.
4. The stretchable nonwoven sheet according to claim 1 wherein the nonwoven sheet has a basis weight between about 40 g/m 2 and about 100 g/m 2 .
5. A personal hygiene garment comprising the stretchable nonwoven sheet of claim 1 .
6. A personal hygiene garment according to claim 5 wherein the garment comprises a diaper.
7. A personal hygiene garment according to claim 5 wherein the garment comprises underwear.
8. A garment comprising the stretchable nonwoven sheet of claim 1 wherein the stretchable nonwoven sheet is an interliner.
9. The stretchable nonwoven sheet according to claim 1 wherein the necked nonwoven substrate has a percent elongation in a cross-direction of between about 100% and about 300%.
10. The stretchable nonwoven sheet according to claim 1 wherein the necked nonwoven substrate has a basis weight between about 15 g/m 2 and about 100 g/m 2 .
11. The stretchable nonwoven sheet according to claim 1 wherein the necked nonwoven substrate has a basis weight between about 15 g/m 2 and about 40 g/m 2 .
12. The stretchable nonwoven sheet according to claim 1 wherein the necked nonwoven substrate has a basis weight between about 30 g/m 2 and about 70 g/m 2 .
13. The stretchable nonwoven sheet according to claim 1 wherein the sheet comprises between about 30 and about 50 weight percent of the elastomeric polymer based on the total weight of elastomeric polymer and nonwoven substrate.
14. The stretchable nonwoven sheet according to claim 1 wherein the elastomeric polymer solution contains dispersed therein fine fibers.