Stabilized environmentally sensitive binders
The present invention relates to environmentally sensitive organic binders stabilized by maleic anhydride and its derivatives. The unstabilized binders can rapidly hydrolyze and thicken when exposed to the environment, and especially to moisture. Maleic anhydride and its derivatives act to stabilize these binders. The stabilized organic binders of the invention are especially useful for forming marine antifoulant coatings.
1 . A stabilized coating composition comprising:
a) one or more environmentally sensitive binders; and
b) 0.1 to 10 percent by weight of one or more stabilizers selected from the group consisting of maleic anhydride or a maleic anhydride derivative.
2 . The stabilized coating composition of claim 1 wherein said binder is an acrylic binder.
3 . The stabilized coating composition of claim 2 wherein said acrylic binder is a silylacrylic binder.
4 . The stabilized coating composition of claim 1 wherein said stabilizer comprises maleic anhydride.
5 . The stabilized coating composition of claim 1 wherein said environmentally sensitive binder is one capable of undergoing hydrolysis.
6 . The stabilized coating composition of claim 1 wherein said stabilizer comprises 0.5 to 5 percent by weight of the coating composition.
7 . The stabilized coating composition of claim 1 wherein said composition comprises a marine anti-fouling coating.
8 . The stabilized coating composition of claim 1 wherein said composition further comprises 0.001-10 wt percent of molecular sieves.
9 . The stabilized coating composition of claim 1 further comprising one or more additives selected from the group consisting of co-binders, rosin, pigments, stabilizers, drying agents, antisagging agents, plasticizers, dispersing agents, thixotropic agents, fillers, biocides, cuprous oxide, and organic co-biocides.
10 . A structure exposed to a marine, freshwater, brackish water, or high humidity environment comprising a substrate having directly coated thereon a coating composition comprising one or more environmentally sensitive binders; and from 0.1 to 10 percent by weight of one or more stabilizers selected from the group consisting of maleic anhydride or a maleic anhydride derivative.