Antibacterial deodorant
Present invention provides an antibacterial deodorant with antibacterial characteristics and high deodorizing capability. The antibacterial deodorant is inorganic oxide particles comprising a metal component and an inorganic oxide other than the metal component, the inorganic oxide includes titanium oxide and silica and/or zirconia, and the titanium oxide is crystalline titanium oxide. A content of the metal component in the inorganic oxide particles is in a range from 0.1 to 30% by weight as converted to an oxide thereof, and an average particle diameter of the inorganic oxide particle is in a range from 2 to 500 nm.
1. An antibacterial deodorant formed of inorganic particles comprising:
a metal component having an antibacterial activity and odor-eliminating activity, said metal component being selected from the group consisting of silver, copper and zinc, and
an inorganic oxide other than said metal component,
wherein said inorganic oxide comprises crystalline titanium oxide, and at least one of silica and zirconia, which form complex inorganic oxide particles,
wherein a content of the metal component in the inorganic oxide particles is in a range from 0.1 to 30% by weight as converted to an oxide thereof,
wherein an average particle diameter of said inorganic oxide particle is in a range from 2 to 500 nm,
wherein the crystalline titanium oxide is presented in a range of 50-90% by weight,
wherein the silica is present in a range of 0-30% by weight, and
wherein the zirconia is present in a range of 0-30% by weight.
2. The antibacterial deodorant according to claim 1 , wherein said titanium oxide is anatase-type titanium oxide.
3. The antibacterial deodorant according to claim 2 , wherein a crystallite diameter of said anatase-type titanium oxide is 100 {acute over (Å)} or more.
4. An antibacterial deodorant formed of a dispersion liquid of inorganic oxide particles comprising;
a metal component having an antibacterial activity and odor-eliminating activity, said metal component being selected from the group consisting of silver, copper and zinc, and
an inorganic oxide other than said metal component with the inorganic oxide dispersed in the dispersion liquid,
wherein said inorganic oxide comprises crystalline titanium oxide, and at least one of silica and zirconia, which form complex inorganic oxide particles,
wherein a content of said metal component in the inorganic oxide particles is in a range from 0.1 to 30% by weight as converted to an oxide thereof,
wherein an average particle diameter of said inorganic oxide particles is in a range from 2 to 500 nm and a concentration of the inorganic oxide particles is in a range from 1 to 20% by weight as converted to an oxide thereof,
wherein said inorganic oxide particles are colloidal particles of the inorganic oxide,
wherein the crystalline titanium oxide is presented in a range of 50-90% by weight,
wherein silica is present in a range of 0-30% by weight, and
wherein zirconia is present in a range of 0-30% by weight.
5. The antibacterial deodorant according to claim 4 , wherein said titanium oxide is anatase-type titanium oxide.
6. The antibacterial deodorant according to claim 5 , wherein a crystallite diameter of said anatase-type titanium oxide is 100 {acute over (Å)} or more.
7. The antibacterial deodorant according to claim 1 , wherein said inorganic oxide comprises said crystalline titanium oxide, silica and zirconia.
8. The antibacterial deodorant according to claim 7 , wherein said metal composition comprises copper.
9. The antibacterial deodorant according to claim 4 , wherein said inorganic oxide comprises said crystalline titanium oxide, silica and zirconia.
10. The antibacterial deodorant according to claim 9 , wherein said metal composition comprises copper.
11. An antibacterial deodorant comprising:
metal particles selected from the group consisting of silver, copper and zinc, and having an antibacterial activity and odor-eliminating activity, and
inorganic oxide particles comprising crystalline titanium oxide, and at least one of silica and zirconia, in a form of complex inorganic oxide particles,
wherein a content of the metal component in the inorganic oxide particles is in a range from 0.1 to 30% by weight as converted to an oxide thereof,
wherein an average particle diameter of said inorganic oxide particle is in a range from 2 to 500 nm,
wherein the crystalline titanium oxide is presented in a range of 50-90% by weight,
wherein the silica is present in a range of 0-30% by weight, and
wherein the zirconia is present in a range of 0-30% by weight.