Pressure-sensitive adhesive with dual crosslinking mechanism
View Patent ↗A process for preparing a polyacrylate-based shaped article, a polyacrylate being polymerized by a conventional method, wherein the polyacrylate comprises copolymerized comonomers having thermally crosslinkable groups and comonomers having attached photoinitiators, and the polyacrylate is crosslinked thermally in a first step and by irradiation with UV light in a second step.
1. A process for preparing a polyacrylate-based shaped article, said process comprising the following steps:
a) forming a polyacrylate by copolymerizing comonomers having thermally crosslinkable groups and comonomers having attached photoinitiators,
b) thermally crosslinking the polyacrylate formed, and subsequently
c) crosslinking the polyacrylate by irradiation with UV light.
2. The process as claimed in claim 1 , wherein the shaped article is of two-dimensionally flat extent.
3. The process as claimed in claim 1 , wherein the polyacrylate is a polyacrylate pressure-sensitive adhesive.
4. The process as claimed in claim 3 , wherein following polymerization the polyacrylate pressure-sensitive adhesive is coated from the melt onto a permanent or temporary backing and the crosslinking steps take place after the coating operation.
5. The process as claimed in claim 3 , wherein the polyacrylate pressure-sensitive adhesive prior to the crosslinking steps has a weight-average molecular weight of not more than 500 000 g/mol.
6. The process as claimed in claim 4 , wherein the polyacrylate pressure-sensitive adhesive in the melt has a residual solvent fraction of not more than 1%.
7. The process as claimed in claim 2 , wherein the polyacrylate is a polyacrylate pressure-sensitive adhesive.
8. The process as claimed in claim 7 , wherein following polymerization the polyacrylate pressure-sensitive adhesive is coated from the melt onto a permanent or temporary backing and the crosslinking steps take place after the coating operation.
9. The process as claimed in claim 7 , wherein the polyacrylate pressure-sensitive adhesive prior to the crosslinking steps has a weight-average molecular weight of not more than 500 000 g/mol.
10. The process as claimed in claim 8 , wherein the polyacrylate pressure-sensitive adhesive in the melt has a residual solvent fraction of not more than 1%.