Processes for preparing crosslinker-free, biopolymer-containing three dimensional structures, and products prepared thereby
Processes for preparing crosslinker-free, chitosan-containing compositions, comprising: (a) providing an aqueous mixture of a chitosan, wherein the aqueous mixture has a viscosity of from 1,000 mPas to 100,000 mPas; (b) combining a precipitant with the aqueous mixture to form a crosslinker-free chitosan composition; and (c) drying the crosslinker-free chitosan composition to form a crosslinker-free three-dimensional structure; are described. Also described are three-dimensional structures prepared thereby and uses therefor in cosmetics, food additives and medical products
1 . A process for preparing a crosslinker-free composition, said process comprising:
(a) providing an aqueous mixture of a chitosan, wherein the aqueous mixture has a viscosity of from 1,000 mPas to 100,000 mPas;
(b) combining a precipitant with the aqueous mixture in an amount and at a rate sufficient to precipitate the chitosan such that a crosslinker-free chitosan composition having physically entangled strands of the chitosan is formed; and
(c) drying the crosslinker-free chitosan composition to form a crosslinker-free three-dimensional structure.
2 . The process according to claim 1 , wherein the aqueous mixture is present in a state selected from the group consisting of solutions and homogenous suspensions.
3 . The process according to claim 1 , wherein the chitosan is present in an amount of from 0.1 to 15% by weight, based on the aqueous mixture.
4 . The process according to claim 1 , wherein the aqueous mixture has a pH value of from 1 to 7.5.
5 . The process according to claim 1 , wherein the aqueous mixture has a viscosity of from 10,000 mPas to 40,000 mPas.
6 . The process according to claim 1 , wherein the chitosan comprises a cationically-derivatized chitosan.
7 . The process according to claim 1 , wherein the precipitant comprises an aqueous solution selected from the group consisting of aqueous solutions of hydrogen carbonates, carbonates, hydrogen phosphates, hydroxides of alkali metals, alkaline earth metals, ammonia and organic nitrogen bases, and combinations thereof.
8 . The process according to claim 1 , wherein the precipitant comprises an aqueous solution of sodium hydrogen carbonate.
9 . The process according to claim 1 , wherein the crosslinker-free chitosan composition formed in step (b) has a pH value of from 5 to 14.
10 . The process according to claim 1 , wherein the drying of the crosslinker-free chitosan composition comprises freeze-drying.
11 . The process according to claim 1 , further comprising combining one or more auxiliaries or additives with the aqueous mixture prior to drying.
12 . The process according to claim 1 , further comprising combining one or more auxiliaries or additives with the crosslinker-free composition subsequent to drying.
13 . A process for preparing a crosslinker-free composition, said process comprising:
(a) providing an aqueous mixture of a cationically-derivatized chitosan, wherein the aqueous mixture has a viscosity of from 10,000 mPas to 40,000 mPas and a pH value of from 1 to 7.5;
(b) combining a precipitant selected from the group consisting of aqueous solutions of hydrogen carbonates, carbonates, hydrogen phosphates, hydroxides of alkali metals, alkaline earth metals, ammonia and organic nitrogen bases, and combinations thereof, with the aqueous mixture in an amount and at a rate sufficient to precipitate the chitosan such that a crosslinker-free chitosan composition having physically entangled strands of the chitosan is formed; and
(c) freeze-drying the crosslinker-free chitosan composition to form a crosslinker-free three-dimensional structure.
14 . A crosslinker-free, chitosan composition prepared by the process according to claim 1 .
15 . A crosslinker-free, chitosan composition prepared by the process according to claim 5 .
16 . A crosslinker-free, chitosan composition prepared by the process according to claim 7 .
17 . A crosslinker-free, chitosan composition prepared by the process according to claim 10 .
18 . A crosslinker-free, chitosan composition prepared by the process according to claim 13 .
19 . A cosmetic preparation comprising a crosslinker-free, chitosan composition prepared by the process according to claim 1 .
20 . A food additive comprising a crosslinker-free, chitosan composition prepared by the process according to claim 1 .
21 . A process for preparing a crosslinker-free composition, said process comprising:
(a) providing an aqueous mixture of a chitosan, wherein the aqueous mixture has a viscosity of from 1,000 mPas to 100,000 mPas;
(b) combining a precipitant with the aqueous mixture in an amount and at a rate sufficient to precipitate the chitosan such that a crosslinker-free chitosan composition having physically entangled strands of the chitosan is formed;
(c) allowing the crosslinker-free chitosan composition to stand, without mixing, for 10 minutes to 10 hours; and
(d) drying the crosslinker-free chitosan composition to form a crosslinker-free three-dimensional chitosan structure.
22 . A process for preparing a crosslinker-free chitosan composition, said process comprising:
(a) providing an aqueous mixture of a chitosan, wherein the aqueous mixture has a viscosity of from 1,000 mPas to 100,000 mPas;
(b) precipitating a crosslinker-free chitosan composition having physically entangled strands of the chitosan by adding a precipitant to the aqueous mixture in an amount and at a rate sufficient to precipitate said crosslinker-free composition; and
(c) forming a crosslinker-free three-dimensional structure by drying the resulting crosslinker-free chitosan composition.