New process of making permanent acid stain resistance for a lightly dyed polyamide carpet
The invention provides a process for making permanent stain resistant polyamide carpets with light color. The process comprises dyeing a low amine end and cationic dyeable polyamide carpet with acid dyes, and imparting stain resist compositions onto the carpet. In addition to stain resist compositions, a fluoro-chemical is also applied to improve soil resistance. The resulted carpet displays a built-in permanent anti-stain and anti-soil resistance after many shampoo-washes.
1 . A process for making permanent acid stain resistant polyamide carpet comprising:
(a) melting a cationic dyeable polyamide copolymer with low amine ends;
(b) spinning the copolymer melt into a yarn;
(c) heating set the yarn on superba with steam;
(d) tufting the heat-set yarn into a carpet;
(e) spraying acid dyes on the carpet;
(f) steaming, and rinsing the carpet;
(g) adding stain resist compositions on the carpet after rinsing; and
(h) steaming, rinsing, and drying the carpet.
2 . The process of claim 1 , wherein the amine ends is about 12 to about 18 per million gram of polyamide yarn.
3 . The process of claim 1 , wherein the heat-set is performed at temperatures of 110 to 140° C.
4 . The process of claim 1 , wherein step (e) is performed at a ph of about 3 to about 5.
5 . The process of claim 1 , wherein the carpet so produced has a color 1 value at least 60.
6 . The process of claim 1 , wherein the carpet so produced has a color 1 value at least 70.
7 . The process of claim 1 , wherein step (g) is performed at a ph of about 1.5 to about 5.0.
8 . The process of claim 1 , wherein the stain resist composition is selected from the group consisting of sulfonated phenol-aldehyde condensation products, and sulfonated naphthol condensation product
9 . The process of claim 1 , wherein the stain resist composition is selected from the group consisting of sulfonated phenol-aldehyde condensation products, and sulfonated naphthol condensation produ, polymethacrylic acid polymers, acrylic acid polymers, copolymers of acrylic acid or methacrylic acid with ethylenically unsaturated comonomers, and hydrolyzed maleic anhydride copolymer with ethylenically unsaturated comonomers.
10 . The process of claim 1 , wherein a fluorochemical is added into step (g).
11 . The process of claim 10 , wherein step (g) is performed at a ph of about 0.8 to about 2.5.
12 . The process of claim 10 , wherein the fluorochemical is selected from the groups consisting of a flurocarbonyllimino biuret, a fluroester, a fluoroester carbamate, and a fluoropolymer.
13 . A uniformly lightly colored carpet made from a cationic dyeable polyamide fiber with low amine ends having a built-in permanent anti-stain resistance according to the process of claim 1 .
14 . A process for making permanent acid stain resistant polyamide carpet comprising:
(a) melting a cationic dyeable polyamide copolymer with low amine ends;
(b) spinning the copolymer melt into a yarn;
(c) heating set the yarn on superba with steam;
(d) tufting the heat-set yarn into a carpet;
(e) spraying a mixture of acid dyes and stain resist compositions on the carpet; and
(f) steaming, rinsing, and drying the carpet.
15 . The process of claim 14 , wherein the amine ends is about 12 to about 18 per million gram of polyamide yarn.
16 . The process of claim 14 , wherein the heat-set is performed at temperatures of 110 to 140° C.
17 . The process of claim 14 , wherein step (e) is performed at a ph of about 1.0 to about 3.0.
18 . The process of claim 14 , wherein the carpet so produced has a color 1 value at least 60.
19 . The process of claim 14 , wherein the carpet so produced has a color 1 value at least 70.
20 . The process of claim 14 , wherein the stain resist composition is selected from the group consisting of sulfonated phenol-aldehyde condensation products, and sulfonated naphthol condensation product.
21 . The process of claim 14 , wherein the stain resist compositions is selected from the group consisting of sulfonated phenol-aldehyde condensation products, and sulfonated naphthol condensation product. Polymethacrylic acid polymers, acrylic acid polymers, copolymers of acrylic acid or methacrylic acid with ethylenically unsaturated comonomers, and hydrolyzed maleic anhydride copolymer with ethylenically unsaturated comonomers.
22 . The process of claim 14 , wherein a flurochemical is added into step (e).
23 . The process of claim 22 , wherein step (e) is performed at a ph of about 0.8 to about 2.5.
24 . The process of claim 22 , wherein the fluorochemical is selected from the groups consisting of a flurocarbonyllimino biuret, a fluroester, a fluoroester carbamate, and a fluoropolymer.
25 . A uniformly lightly colored carpet made from a cationic dyeable polyamide fiber with low amine ends having a built-in permanent anti-stain resistance according to the process of claim 14.