Support for electrophotographic image receiving sheet and electrophotographic image recording sheet
A support for an image recording paper comprises a support paper and a coating layer formed on one surface thereof on which an image is formed. The coating layer is formed by a film of polypropylene having a density less than 0.88 g/cm 3 . An image recording paper comprises the support and an image recording layer formed over the coating layer.
1 . An image recording paper support comprising:
a support paper; and
a coating layer formed on at least one surface of said support paper on which an image is formed;
wherein said coating layer contains a propylene resin having a density less than 0.88 g/cm 3 .
2 . The image recording sheet support as defined in claim 1 , wherein said propylene resin is amorphous.
3 . The image recording sheet support as defined in claim 2 , wherein said coating layer formed on said one surface of said support paper has a polypropylene resin content greater than 5% by mass.
4 . The image recording sheet support as defined in claim 1 , wherein said propylene resin is selected from a group consisting of a polypropylene resin, copolymers of propylene and ethylene and copolymers of propylene and butene.
5 . The image recording sheet support as defined in claim 1 , wherein said coating layer formed on said one surface of said support paper has a polypropylene resin content greater than 5% by mass.
6 . The image recording sheet support as defined in claim 1 , wherein said coating layer formed on said one surface of said support paper further contains a crystalline propylene resin.
7 . The image recording sheet support as defined in claim 6 , wherein a crystalline propylene resin content of said coating layer is less than 95% by mass.
8 . The image recording sheet support as defined in claim 1 , wherein said propylene resin has a met flow rate in a range of from 0.5 to 6 g/10 seconds at 230° C.
9 . The image recording sheet support as defined in claim 1 , wherein said support paper has a density in a range of from 0.85 to 1.15 g/cm 3 .
10 . The image recording sheet support as defined in claim 1 , wherein said support paper is pressure dried before application of said coating layer.
11 . The image recording sheet support as defined in claim 10 , wherein said support paper is calendered before application of said coating layer.
12 . The image recording sheet support as defined in claim 11 , wherein said support paper is calendered with a calender with a metal roll kept at 140° C.
13 . The image recording sheet support as defined in claim 1 , wherein said support paper is used as printing paper.
14 . An image recording paper support comprising:
a support paper; and
a coating layer formed on at least one surface of said support paper on which an image is formed;
wherein said coating layer contains an amorphous polyolefin resin.
15 . The image recording sheet support as defined in claim 14 , wherein said amorphous polyolefin resin comprises a propylene resin.
16 . The image recording sheet support as defined in claim 5 , wherein said amorphous polyolefin resin has a met flow rate in a range of from 0.5 to 6 g/10 seconds at 230° C.
17 . The image recording sheet support as defined in claim 16 , wherein said coating layer formed on said one surface of said support paper further contains a crystalline propylene resin.
18 . The image recording sheet support as defined in claim 17 , wherein a crystalline propylene resin content of said coating layer is less than 95% by mass.
19 . The image recording sheet support as defined in claim 16 , wherein said propylene resin has a met flow rate in a range of from 0.5 to 6 g/10 seconds at 230° C.
20 . The image recording sheet support as defined in claim 16 , wherein said support paper has a density in a range of from 0.85 to 1.15 g/cm 3 .
21 . The image recording sheet support as defined in claim 14 , wherein said support paper is pressure dried before application of said coating layer.
22 . The image recording sheet support as defined in claim 21 , wherein said support paper is calendered before application of said coating layer.
23 . The image recording sheet support as defined in claim 22 , wherein said support paper is calendered with a calender with a metal roll kept at 140° C.
24 . The image recording sheet support as defined in claim 14 , wherein said support paper is used as printing paper.
25 . An image recording paper comprising said image recording paper support as defined in any one of the preceding claims 1 through 24 and an image recording layer.
26 . The image recording paper as defined in claim 25 , wherein said image recording layer is formed on said one surface.
27 . The image recording paper as defined in claim 25 , wherein said image recording layer comprises a resin coating layer.
28 . The image recording paper as defined in claim 25 , and further comprising an intermediate layer between said image recording paper support and said image recording layer.
29 . The image recording paper as defined in claim 28 , wherein said intermediate layer comprises a resin coating layer.
30 . The image recording paper as defined in claim 28 , wherein said resin coating layer is formed by applying a coating liquid of aqueous polymer.
31 . The image recording paper as defined in claim 30 , wherein said aqueous polymer comprises either one of a water-dispersant polyester resin and a water-dispersant acryl resin.
32 . The image recording sheet support as defined in claim 25 , wherein said image recording paper is used as at least one of electrophotographic printing paper, heat sensitive printing paper, sublimatic transfer printing paper, thermal development printing paper, silver halide photographic printing paper and ink-jet printing paper.