View Patent ↗A calcium phosphate cement suitable for use in dental and bone prosthesis is disclosed, which include calcium phosphate particles having a diameter of 0.05 to 100 microns, wherein said calcium phosphate particles on their surfaces have whiskers or fine crystals having a width ranging from 1 to 100 nm and a length ranging from 1 to 1000 nm.
1. A method of repairing a defect or a cavity in a bone or a tooth comprising:
forming a non-dispersive, injectable calcium phosphate cement paste by contacting calcium phosphate cement particles with an aqueous solution comprising a hardening-promoter; and
injecting the paste into the defect or the cavity in the bone or tooth;
wherein the diameter of the calcium phosphate cement particles is from 0.05 microns to 100 microns, wherein at least a portion of the calcium phosphate particles have surface crystals comprising basic calcium phosphate crystals, and wherein the surface crystals have a width ranging from 1 nm to 100 nm and a length ranging from 1 to 1000 nm.
2. The method of claim 1 , wherein the calcium phosphate cement particles comprise calcium dihydrogen phosphate, calcium dihydrogen phosphate hydrate, acid calcium pyrophosphate, anhydrous calcium hydrogen phosphate, tetracalcium phosphate, calcium hydrogen phosphate hydrate, calcium pyrophosphate, calcium triphosphate, calcium polyphosphate, calcium metaphosphate, anhydrous tricalcium phosphate, tricalcium phosphate hydrate, apatite, hydroxyapatite, or mixtures thereof.
3. The method of claim 1 , wherein the calcium phosphate cement particles comprise dicalcium phosphate anhydrous, tetracalcium phosphate, tricalcium phosphate, or mixtures thereof.
4. The method of claim 1 , wherein the paste further comprises a growth factor, a bone morphology protein, a pharmaceutical carrier, or mixtures thereof.
5. The method of claim 1 , wherein the hardening-promoter comprises phosphate ions, calcium ions, fluorine ions, or mixtures thereof.
6. The method of claim 1 , wherein the aqueous solution comprises 1 mM to 3 M of the hardening promoter.
7. The method of claim 1 , wherein hardening-promoter comprises phosphate ions.
8. The method of claim 1 , wherein the pH of the aqueous solution is 6.0.
9. The method of claim 1 , wherein the calcium phosphate cement particles have a diameter ranging from 0.5 microns to 50 microns.
10. The method of claim 1 , wherein the crystals have a length ranging from 10 nm to 700 nm.
11. The method of claim 1 , wherein the calcium phosphate cement particles have a calcium to phosphate molar ratio ranging from 0.5 to 2.5.
12. The method of claim 1 , wherein the calcium phosphate cement particles have a calcium to phosphate molar ratio ranging from 0.8 to 2.3.
13. The method of claim 1 , wherein the calcium phosphate cement particles have a calcium to phosphate molar ratio ranging from 1.0to 2.2.