Process by producing an aluminium alloy brazing sheet, aluminium alloy brazing sheet
View Patent ↗Disclosed is a process for producing an Al—Mn alloy sheet with improved liquid film migration resistance when used as core alloy in brazing sheet, including the steps of: casting an ingot having a composition comprising (in weight percent): 0.5<Mn≦1.7, 0.06<Cu≦1.5, Si≦1.3, Mg≦0.25, Ti<0.2, Zn≦2.0, Fe≦0.5, at least one element of the group of elements of 0.05<Zr≦0.25 and 0.05<Cr≦0.25; other elements <0.05 each and total <0.20, balance Al; homogenisation and preheat; hot rolling; cold rolling (including intermediate anneals whenever required), and wherein the homogenisation temperature is at least 450° C. for a duration of at least 1 hour followed by an air cooling at a rate of at least 20° C./h and wherein the pre-heat temperature is at least 400° C. for at least 0.5 hour.
1. Process for producing an Al—Mn alloy sheet with improved liquid film migration resistance when used as core alloy in brazing sheet, comprising the steps of:
casting a composition comprising (in weight percent):
0.5<Mn≦1.7
0.06<Cu≦1.5
Si≦1.3
Mg≦0.25
Ti<0.2
Zn≦2.0
Fe≦0.5
0.05<Cr≦0.12 and Zr<0.01,
other elements <0.05 each and total <0.20, balance Al.
homogenisation and preheat
hot rolling
cold rolling (including intermediate anneals whenever required), and wherein the homogenisation temperature is at least 450° C. for a duration of at least 1 hour followed by an air cooling at a rate of at least 20° C./h and wherein the pre-heat temperature is at least 400° C. for at least 0.5 hour.
2. Process according to claim 1 , wherein the homogenisation temperature is between about 530° C. and 620° C. for between 1 to 25 hours, and wherein the pre-heat temperature is between about 400° C. and 530° C. for between 1 to 25 hours.
3. Process according to claim 1 , wherein Si≦0.8%.
4. Process according to claim 1 , wherein Si≦0.3%.
5. Process according to claim 1 , wherein Si≦0.15%.
6. Process according to claim 1 , wherein Mn is in between 0.7 and 1.4%.
7. Process according to claim 1 , wherein 0.08<Cr≦0.12.
8. Process according to claim 1 , wherein Mg≦0.15%.
9. Process according to claim 1 , wherein Mg≦0.05%.
10. Process according to claim 1 , wherein preferably Zn≦0.4%.
11. Process according to claim 1 , further comprising cladding the Al—Mn alloy on at least one side with an Al—Si brazing alloy optionally comprising up to 2.0% Zn.
12. Process according to claim 1 , further comprising cladding the Al—Mn alloy on at least one side with an Al—Si brazing alloy optionally comprising up to 2.0% Zn, and having a non-brazing liner alloys such as AA7072 or AA1145 or AA3005 or Al—Mn type alloys containing Zn in the range 0.5-5.0%.
13. Process according to claim 1 , further comprising cladding the Al—Mn alloy on at least one side with an Al—Si brazing alloy optionally comprising up to 2.0% Zn, and having a non-brazing liner alloys such as AA7072 or AA1145 or AA3005 or Al—Mn type alloys containing Zn in the range 0.5-2.5%.
14. Process according to claim 1 , further comprising V 0.05-0.25 wt. %.
15. Process according to claim 1 , wherein the sum of Cr, Zr, and V is 0.05-0.25 wt. %.
16. Sheet produced according to claim 1 , wherein the pre-braze elongation is at least 18%.
17. Sheet produced according to claim 1 , wherein the pre-braze elongation is at least 19%.
18. Sheet according to claim 16 , wherein the post-brazing tensile strength is at least 140 MPa.
19. Sheet according to claim 16 , wherein the post-brazing tensile strength is at least 150 MPa.
20. Sheet according to claim 16 , wherein the pre-braze n-value is at least 0.270.
21. Sheet according to claim 16 , wherein the post-braze coupon SWAAT lifetime, when tested according to ASTM G85 A3, is at least 15 days without perforation.
22. Method of use of sheet produced according to claim 1 , comprising combining the sheet as a core alloy with cladding to form a brazing sheet intended for manufacturing of components of tube-fin type heat exchangers such as radiators, heater cores and condensers.
23. Method of use of sheet produced according to claim 1 , comprising combining the sheet as a core alloy with cladding to form a brazing sheet intended for manufacturing of components of plate-fin type heat exchanger such as evaporator or oil cooler core plates or tanks of radiators or heater cores.
24. Method of use of sheet produced according to claim 1 , comprising combining the sheet as a core alloy with cladding to form brazing fin stock materials intended for manufacturing of components for heat exchangers.
25. Brazing sheet comprising the sheet according to claim 16 , as a core alloy combined with cladding to form a brazing sheet intended for manufacturing of components of tube-fin type heat exchangers such as radiators, heater cores and condensers.
26. Brazing sheet comprising the sheet according to claim 16 , as a core alloy combined with cladding to form a brazing sheet intended for manufacturing of components of plate-fin type heat exchanger such as evaporator or oil cooler core plates or tanks of radiators or heater cores.
27. Brazing sheet comprising the sheet according to claim 16 , as a core alloy combined with cladding to form brazing fin stock materials intended for manufacturing of components for heat exchangers.
28. Process according to claim 1 , wherein 0.72<Cu≦1.5.
29. Process according to claim 1 , wherein 0.80<Cu≦1.5.