Method of making fibers and nonwovens with improved properties
View Patent ↗The present invention can provide a distinctive method and process for making polymer fibers ( 62 ) and nonwoven fabric webs ( 60 ). The method can include providing a fiber material that exhibits a low crystallization rate. In a particular aspect, the fiber material can be subjected to an anneal-quench at an anneal-quench temperature that approximates a prime-temperature at which the polymer material most rapidly crystallizes. In another aspect, the fiber material can be subjected to a fiber-draw at a selected fiber-draw temperature, and in a further aspect, the fiber-draw temperature can be configured to approximate the prime-temperature of the polymer material. In still other aspects, the fiber material can be subjected to a relatively small amount of fiber-draw, and the fiber-draw can be provided at a relatively low fiber-draw speed.
1. A method of making thermoplastic polymer fibers, the method comprising: a) providing a thermoplastic polymer material that exhibits a slow crystallization rate; b) forming a plurality of molten polymer fibers from said thermoplastic polymer material; c) subjecting said molten polymer fibers immediately upon extrusion to anneal-quenching at an anneal-quench temperature that is at least 10° C. greater than the glass transition temperature (Tg) of said thermoplastic polymer material but less than a melting temperature thereof, and which approximates a prime temperature at which can achieve an amount of crystallinity in the thermoplastic polymer material of about 45% or greater as determined by differential scanning calorimetry (DSC).
2. The method according to claim 1 , further comprises subjecting immediately the anneal-quenched polymer fibers to a fiber-draw at a draw temperature which is not more than 30° C. either higher or lower than said prime-temperature.
3. The method according to claim 2 , wherein said fiber-draw temperature approximates said prime temperature.
4. The method according to claim 1 , wherein said anneal-quenching is by means of a gas or air that has been heated to the anneal-quench temperature.
5. The method according to claim 1 , wherein said thermoplastic polymer material exhibits a crystallization half-time value which is not less than about 300 sec, as determined by differential scanning calorimetry.
6. The method according to claim 1 , wherein the anneal-quench temperature is not more than either 30° C. higher or lower than the prime-temperature.
7. The method according to claim 2 , wherein the anneal-quenched polymer fiber material is subjected to a fiber-draw which provides a fiber draw down ratio of about 3000 or less.
8. The method according to claim 2 , further includes depositing the anneal-quenched polymer fibers on an operative forming surface to produce a nonwoven fabric; and moving the forming surface at a surface speed of not more than about 1500 msec.
9. The method according to claim 2 , wherein said the anneal-quenched polymer fibers is subject to a pneumatic fiber-draw.
10. The method according to claim 2 , wherein the fiber-draw temperature is provided by an application of heated gas during the fiber-draw.
11. The method according to claim 2 , wherein said anneal-quenched polymer fibers have a fiber size of not more than a maximum of about 30 μm.
12. The method according to claim 1 , wherein the thermoplastic polymer material includes a base material that includes: a) a blend of polylactic acid polymers; b) a blend of polylactic acid copolymers; or c) a combination of a) and b).
13. The method according to claim 12 , wherein said base material includes at least about 95 wt % of polylactic acid polymer.
14. The method according to claim 12 , wherein the base material has been provided by admixing a base polymer with an operative amount of a plasticizer.
15. The method according to claim 14 , wherein the amount of plasticizer is not more than about 10% by weight.
16. The method according to claim 12 , wherein the base material has been provided by admixing the base polymer with an operative amount of a nucleating agent.
17. The method according to claim 16 , wherein the amount of nucleating agent is up to about 5 wt %.
18. A method of forming a fiberous web, the method comprising: a) providing a thermoplastic polymer material from a melt b) forming said thermoplastic polymer material into a plurality of molten fiber material; and c) subjecting said polymer fiber material immediately upon extrusion to an anneal-quenching that is conducted before or during a solidification of the polymer fiber material from its molten state, wherein the polymer fiber material are subjected to an anneal-quench temperature that is at least 10° C. greater than the glass transition temperature (Tg) of said thermoplastic polymer material, up to a maximum of about 125° C.
19. The method according to claim 18 , wherein said anneal-quench temperature is either not more than 30° C. higher or lower than a prime-temperature.
20. The method according to claim 18 , further comprises subjecting said anneal-quenched polymer fiber material to a fiber draw-down ratio of about 3000 or less; and depositing a plurality of fibers on a moving forming surface to form a fibrous web.