Catalyst composition and process using same
A catalyst composition including a solution of at least one member selected from the group consisting of an alkali metal carboxylate and an alkaline earth metal carboxylate in a solvent which is nonreactive with the isocyanate groups of a polyisocyanate.
1. A polyurethane or polyisocyanurate formulation comprising from about 0.3 percent to about 10 percent based on the total weight of the polyurethane or polyisocyanurate formulation of a catalyst composition, the catalyst composition comprising a solution comprising (a) at least one of a carboxylate chosen from an alkali metal carboxylate and an alkaline metal carboxylate, (b) a solvent that is nonreactive with the isocyanate groups of a polyisocyanate, and (c) water present in an amount of less than 25 percent by weight of the catalyst composition, wherein the solvent comprises an adipate is present in an amount of less than about 90 percent by weight of the catalyst composition.
2. A polyurethane or polyisocyanurate formulation using from about 0.3 percent to about 10 percent based on the total weight of a polyurethane or polyisocyanurate formulation of a catalyst composition, the catalyst composition comprising a solution comprising (a) at least one of a carboxylate chosen from an alkali metal carboxylate and an alkaline metal carboxylate, and (b) a solvent that is nonreactive with the isocyanate groups of a polyisocyanate, wherein the carboxylate is lithium caprylate, sodium caprylate, potassium caprylate, calcium caprylate, lithium 2-ethylhexanoate, sodium 2-ethylhexanoate, calcium 2-ethylhexanoate or potassium 2-ethylhexanoate, and the solvent comprises an adipate.
3. A polyurethane foam containing urethane and isocyanurate groups obtained by reacting at least one polyisocyanate with at least one compound having at least two isocyanate-reactive hydrogen atoms in the presence of a catalyst composition having a solution comprising (a) at least one member selected from the group consisting of an alkali metal carboxylate and an alkaline earth metal carboxylate, and (b) a solvent which is nonreactive with the isocyanate groups of the polyisocyanate, wherein the solvent comprises an adipate.
4. A polyurethane or polyisocyanurate formulation comprising from about 0.3 percent to about 10 percent based on the total weight of the polyurethane or polyisocyanurate formulation of a catalyst composition, the catalyst composition comprising a solution comprising (a) at least one carboxylate, (b) a solvent that is nonreactive with the isocyanate groups of a polyisocyanate, and (c) water present in an amount of less than 25 percent by weight of the catalyst composition, wherein the at least one carboxylate includes at least potassium 2-ethylhexanoate, the solvent comprises at least polyethylene glycol di-2-ethylhexanoate, and the solvent is present in an amount of less than about 90 percent by weight of the catalyst composition.
5. A polyurethane foam containing urethane and isocyanurate groups obtained by reacting at least one polyisocyanate with at least one compound having at least two isocyanate-reactive hydrogen atoms in the presence of a catalyst composition having a solution comprising (a) at least one member selected from the group consisting of an alkali metal carboxylate and an alkaline earth metal carboxylate, and (b) a solvent which is nonreactive with the isocyanate groups of the polyisocyanate, wherein the at least one carboxylate includes at least potassium 2-ethylhexanoate, and the solvent comprises at least polyethylene glycol di-2-ethylhexanoate.