Process for producing continuous filament nonwoven fabric
The present invention is directed to a process for producing continuous filament nonwoven fabric which comprises the steps of providing a single polymeric resin having an MFR of between about 6 to 16, spinning said single polymeric resin using commercially available continuous filament spinning equipment, to yield a continuous filament nonwoven fabric exhibiting a tensile strength improvement of at least 30% when compared to similar resin of greater than 35 MFR.
1 . A process for producing continuous filament nonwoven fabric, comprising the steps of:
providing a single polypropylene resin having an MFR of about 6 to 16;
providing a spinneret assembly having a plurality of extrusion holes;
elevating the temperature of said polymeric resin to a melt temperature between of about 240° C. to 280° C.;
extruding the polymeric resin through the holes of the spinneret assembly to form filaments at a rate of about 0.4 to 0.7 grams/hole/minute;
drawing said filaments at a rate of between about 1200 to 1800 meters/minute; collecting said filaments to form a nonwoven fabric; and
said nonwoven fabric having a minimum MD and CD Strip Tensile Strength per unit basis weight of at least 47.1 grams-force per centimeter per gram per square meter.
2 . A process for producing continuous filament nonwoven fabric as in claim 1 , wherein said polymeric resin is elevated to a melt temperature of between about 250° C. and 270° C.
3 . A process for producing continuous filament nonwoven fabric as in claim 1 , wherein said filaments are formed at a rate of 0.43 to 0.6 grams/hole/minute.
4 . A process for producing continuous filament nonwoven fabric as in claim 1 , wherein said filaments are drawn at a rate of between about 1400 to 1700 meters/minute.
5 . A process for producing continuous filament nonwoven fabric as in claim 1 , wherein said nonwoven fabric is formed by application of calender rolls at a pressure of about 400 to 800 pounds/linear inch, said drolls having a surface temperature of about 145° C. to 165° C.
6 . A process for producing continuous filament nonwoven fabric, comprising the steps of:
providing a polymeric resin consisting of a single polypropylene polymer having an MFR of about 6 to 16;
providing a spinneret assembly having a plurality of extrusion holes;
elevating the temperature of said polymeric resin to a melt temperature between of about 240° C. to 280° C.;
extruding the polymeric resin through the holes of the spinneret assembly to form filaments at a rate of about 0.4 to 0.7 grams/hole/minute;
drawing said filaments at a rate of between about 1200 to 1800 meters/minute; collecting said filaments to form a nonwoven fabric; and
said nonwoven fabric having a minimum MD and CD Strip Tensile Strength per unit basis weight of at least 47.1 grams-force per centimeter per gram per square meter.
7 . A continuous filament nonwoven fabric, comprising a polypropylene resin having an MFR of about 6 to 16, said nonwoven fabric having a minimum MD and CD Strip Tensile Strength per unit basis weight of at least 47.1 grams-force per centimeter per gram per square meter.
8 . (canceled)