Hexagonal ferrite magnetic powder, method for producing the same and magnetic recording medium
View Patent ↗A hexagonal ferrite magnetic powder having an average tabular diameter of from 15 to 28 nm, a coercive force (Hc) of from 2,000 to 5,000 Oe (from 160 to 400 kA/m), a switching field distribution (SFD) of from 0.3 to 0.7 and a D 70 /D 50 of from 1.05 to 1.25. This magnetic powder can be obtained by melting and quenching starting materials to obtain an amorphous product, and thermally treating the product, which comprises increasing a temperature at a rate of 300 to 500° C./hr in a temperature range of 550 to 600° C. in the thermal treatment before the temperature reaches the thermally treating temperature.
1. A hexagonal ferrite magnetic powder having an average tabular diameter of from 15 to 28 nm, a coercive force (Hc) of from 2,000 to 5,000 Oe, a switching field distribution (SFD) of from 0.3 to 0.7 and a D 70 /D 50 of from 1.05 to 1.25.
2. A magnetic recording medium comprising:
a non-magnetic support; and
a magnetic layer containing a hexagonal ferrite magnetic powder dispersed in a binder,
wherein the hexagonal ferrite magnetic powder is a hexagonal ferrite magnetic powder according to claim 1 .
3. The magnetic recording medium according to claim 2 , which further comprises a non-magnetic layer containing a non-magnetic powder dispersed in a binder between the non-magnetic support and the magnetic layer.