Hexagonal ferrite magnetic powder, process for producing the same, and magnetic recording medium
A hexagonal ferrite magnetic powder having an average tabular diameter of from 15 to 30 nm, an average tabular ratio of from 3.0 to 4.9, an Hc of from 2,020 to 5,000 Oe (from 161.6 to 400 kA/m) and an SFD of from 0.3 to 0.7, and comprising at least one tetravalent element in a proportion of from 0.004 to 0.045 atoms based on one atom of Fe.
1 . A hexagonal ferrite magnetic powder having an average tabular diameter of from 15 to 30 nm, an average tabular ratio of from 3.0 to 4.9, an Hc of from 2,020 to 5,000 Oe (from 161.6 to 400 kA/m) and an SFD of from 0.3 to 0.7, and comprising at least one tetravalent element in a proportion of from 0.004 to 0.045 atoms based on one atom of Fe.
2 . The hexagonal ferrite magnetic powder according to claim 1 , wherein the tetravalent element is at least one member selected from the group consisting of Ti, Mn, Zr, Sn, Hf, Ir, Ce and Pb.
3 . The hexagonal ferrite magnetic powder according to claim 1 , wherein the tetravalent element is at least one member selected from the group consisting of Zr and Sn.
4 . The hexagonal ferrite magnetic powder according to claim 1 , further comprising at least one divalent element selected from the group consisting of Mg, Co, Ni, Cu, Zn, Pd and Cd in a proportion of from 0.004 to 0.045 atoms based on one atom of Fe.
5 . The hexagonal ferrite magnetic powder according to claim 1 , further comprising at least one divalent element selected from the group consisting of Mg, Co, Ni, Cu, Zn, Pd and Cd in a proportion of from 0.010 to 0.035 atoms based on one atom of Fe.
6 . The hexagonal ferrite magnetic powder according to claim 1 , further comprising at least one divalent element selected from the group consisting of Co and Zn in a proportion of from 0.004 to 0.045 atoms based on one atom of Fe.
7 . The hexagonal ferrite magnetic powder according to claim 1 , which comprises at least one tetravalent element in a proportion of from 0.010 to 0.035 atoms based on one atom of Fe.
8 . The hexagonal ferrite magnetic powder according to claim 1 , which has an average tabular diameter of from 18 to 28 nm.
9 . The hexagonal ferrite magnetic powder according to claim 1 , which has an average tabular ratio of from 3.0 to 4.2.
10 . The hexagonal ferrite magnetic powder according to claim 1 , which has an Hc of from 2,100 to 4,200 Oe (from 168 to 336 kA/m).
11 . The hexagonal ferrite magnetic powder according to claim 1 , which has an SFD of from 0.3 to 0.6.
12 . A process for producing the hexagonal ferrite magnetic powder according to claim 1 , which comprises:
mixing hexagonal ferrite forming raw materials with at least one tetravalent element in a proportion of from 0.004 to 0.045 atoms based on one atom of Fe contained in the hexagonal ferrite forming raw materials to obtain a mixture;
melting the mixture;
quenching the molten mixture to obtain an amorphous material; and
thermally treating the amorphous material to deposit a hexagonal ferrite.
13 . The process according to claim 12 , wherein the tetravalent element is at least one member selected from the group consisting of Ti, Mn, Zr, Sn, Hf, Ir, Ce and Pb.
14 . A magnetic recording medium comprising:
a non-magnetic support; and
a magnetic layer containing a hexagonal ferrite magnetic powder according to claim 1 and a binder.
15 . The magnetic recording medium according to claim 14 , further comprising a non-magnetic layer between the non-magnetic support and the magnetic layer, the non-magnetic layer containing non-magnetic powder and a binder.