Method for the production of golf ball
View Patent ↗Mold 12 has an upper mold half 14 and a lower mold half 16 . Pellet 34 obtained by cutting a resin composition into a predetermined size is placed into the mold 12 . One pellet 34 is put on one recessed part 24 . The pellet 34 has an incipient fluidization temperature T of 50° C. or greater and 150° C. or less. Weight of the pellet 34 is 1.4 g or greater and 2.0 g or less. Through clamping, the pellet 34 is compressed, and heated to allow the resin composition to flow thereby forming a preforming material. Difference (Tp−T) between the molding temperature Tp and the incipient fluidization temperature T is equal to or less than 70° C. Percent Pp of change in the weight average molecular weight Mp of the preforming material to the weight average molecular weight M of the pellet 34 is equal to or greater than −30%. Cover is formed with this preforming material. Percent Pc of change in the weight average molecular weight Mc of the cover to the weight average molecular weight M of the pellet 34 is equal to or greater than −30%.
1. A method of the production of a golf ball which comprises:
preparing a resin composition comprising a thermoplastic resin as a base polymer to obtain a first material; and
covering around a spherical core with said resin composition while allowing said resin composition to flow in a mold to form a cover having a percent Pc of change in molecular weight with respect to the first material of equal to or greater than −30%.
2. The method of the production according to claim 1 , wherein said material has an incipient fluidization temperature of 50° C. or greater and 150° C. or less.
3. The method of the production according to claim 1 , wherein said cover is formed by compression molding, with the molding temperature falling within the range of −20° C. or greater and +70° C. or less than the incipient fluidization temperature of the material, and with the molding time period of the compression molding being 1 minute or longer and 30 minutes or less.
4. A method of the production of a golf ball which comprises:
preparing a resin composition comprising a thermoplastic resin as a base polymer to obtain a first material;
forming a preforming material having a percent Pp of change in molecular weight with respect to the first material of equal to or greater than −30%, while allowing said resin composition to flow in a first mold;
placing said preforming material and a spherical core into a second mold; and
covering around the core with said resin composition while allowing the resin composition of said preforming material to flow in the second mold to form a cover.
5. The method of the production according to claim 4 , wherein said material has an incipient fluidization temperature of 50° C. or greater and 150° C. or less.
6. The method of the production according to claim 4 , wherein said preforming material is formed by compression molding, with the molding temperature falling within the range of −20° C. or greater and +70° C. or less than the incipient fluidization temperature of the material, and with the molding time period of the compression molding being 1 minute or longer and 30 minutes or less.
7. The method of the production according to claim 6 , wherein said material is in a pellet form, and one pellet has a weight of 1.4 g or greater and 2.0 g or less.
8. The method of the production according to claim 4 , wherein said cover has a percent Pc of change in molecular weight with respect to the first material of equal to or greater than −30%.
9. The method of production according to claim 1 , wherein the percent Pc is equal to or greater than −20%.
10. The method of production according to claim 1 , wherein the percent Pc is equal to or greater than −10%.
11. The method of production according to claim 4 , wherein the percent Pp is equal to or greater than −20%.
12. The method of production according to claim 4 , wherein the percent Pp is equal to or greater than −10%.
13. The method of the production according to claim 2 , wherein said material has an incipient fluidization temperature of 50° C. or greater and 140° C. or less.
14. The method of the production according to claim 2 , wherein said material has an incipient fluidization temperature of 50° C. or greater and 135° C. or less.
15. The method of the production according to claim 5 , wherein said material has an incipient fluidization temperature of 50° C. or greater and 140° C. or less.
16. The method of the production according to claim 5 , wherein said material has an incipient fluidization temperature of 50° C. or greater and 135° C. or less.