Porous beta-tricalcium phosphate and methods for producing the same
View Patent ↗Methods are provided for producing porous β-Tricalcium Phosphate (β-TCP). In the subject methods, β-TCP is combined with graphite to produce an intermediate greenware product. The intermediate greenware product is then sintered to produce porous β-TCP. The subject methods and compositions produced thereby find use in a variety of applications.
1. A method of making a porous tricalcium phosphate, said method comprising:
combining a tricalcium phosphate with graphite to produce a graphite containing tricalcium phosphate composition;
heating said graphite containing tricalcium phosphate composition to a sintering temperature in an inert atmosphere; and
sintering said graphite containing tricalcium phosphate composition to produce said porous tricalcium phosphate, wherein said sintering comprises maintaining said composition at said sintering temperature in an oxidizing atmosphere.
2. The method according to claim 1 , wherein said tricalcium phosphate is beta-tricalcium phosphate.
3. The method according to claim 1 , wherein said graphite containing tricalcium phosphate composition is produced by: combining said tricalcium phosphate and said graphite with water to produce a slurry; and dehydrating said slurry to produce said graphite containing tricalcium phosphate composition.
4. The method according to claim 3 , wherein said graphite is made up of graphite compositions of at least two different sizes.
5. The method according to claim 4 , wherein said graphite comprises graphite flakes and graphite particles.
6. The method according to claim 3 , wherein said dehydrating occurs at a pressure greater than atmospheric pressure.
7. The method according to claim 1 , wherein said method further comprises grinding said porous tricalcium phosphate to produce a particulate composition.
8. The method according to claim 1 , wherein said sintering occurs at a temperature ranging from about 1100 to about 1300° C.
9. The method according to claim 8 , wherein said sintering occurs at a temperature of about 1200° C.