Hydrogen-absorbing alloy electrode and alkaline storage battery
View Patent ↗A hydrogen-absorbing alloy for a negative electrode in an alkaline storage battery includes a first hydrogen-absorbing alloy and a second first hydrogen-absorbing alloy. The first hydrogen-absorbing alloy contains at least a rare-earth element, Mg, Ni, and Al, and has an intensity ratio I A /I B of 0.1 or greater in X-ray diffraction analysis using Cu—Kα radiation as an X-ray source, where I A is the strongest peak intensity that appears in the range of 2θ=31° to 33°, and I B is the strongest peak intensity that appears in the range of 2θ=40° to 44°. The second hydrogen-absorbing alloy has a Co content greater than that of the first hydrogen-absorbing alloy.
1. A hydrogen-absorbing alloy electrode comprising:
a first hydrogen-absorbing alloy containing at least a rare-earth element, magnesium, nickel, and aluminum, and cobalt in an amount of 2.0 weight % or less, and having an intensity ratio I A /I B of 0.1 or greater in X-ray diffraction analysis using Cu—Kα radiation as an X-ray source, where I A is the strongest peak intensity that appears in the range of 2θ=31° to 33°, and I B is the strongest peak intensity that appears in the range of 2θ=40° to 44°; and
a second hydrogen-absorbing alloy having a CaCu 5 crystal structure and a cobalt content greater than the first hydrogen-absorbing alloy, and being added to the first hydrogen-absorbing alloy, wherein the second hydrogen-absorbing alloy has a smaller average particle diameter than that of the first hydrogen-absorbing alloy.
2. The hydrogen-absorbing alloy electrode according to claim 1 , wherein the amount of cobalt contained in the second hydrogen-absorbing alloy is 25 weight % or greater with respect to the total amount of cobalt contained in the first hydrogen-absorbing alloy and the second hydrogen-absorbing alloy.
3. The hydrogen-absorbing alloy electrode according to claim 2 , wherein the amount of cobalt contained in the second hydrogen-absorbing alloy is within the range of from 50 to 75 weight % with respect to the total amount of cobalt contained in the first hydrogen-absorbing alloy and the second hydrogen-absorbing alloy.
4. The hydrogen-absorbing alloy electrode according to claim 1 , wherein the amount of the second hydrogen-absorbing alloy is within the range of from 5 to 50 weight % with respect to the total amount of the first hydrogen-absorbing alloy and the second hydrogen-absorbing alloy.
5. The hydrogen-absorbing alloy electrode according to claim 4 , wherein the amount of the second hydrogen-absorbing alloy is within the range of from 15 to 30 weight % with respect to the total amount of the first hydrogen-absorbing alloy and the second hydrogen-absorbing alloy.
6. The hydrogen-absorbing alloy electrode according to claim 1 , wherein the first hydrogen-absorbing alloy is represented by the general formula Ln 1−x Mg x Ni y−a Al a , where Ln is an element selected from rare-earth elements, 0.10≦x≦0.30, 3≦y≦3.6, and 0≦a≦0.3.
7. The hydrogen-absorbing alloy electrode according to claim 6 , wherein, in the hydrogen-absorbing alloy represented by the general formula, a portion or portions of the Ln and/or Ni is substituted by at least one element selected from the group consisting of V, Nb, Ta, Cr, Mo, Mn, Fe, Co, Ga, Zn, Sn, In, Cu, Si, P, and B.
8. An alkaline storage battery, comprising a positive electrode, a negative electrode, a separator, and an alkaline electrolyte solution, the negative electrode being a hydrogen-absorbing alloy electrode according to claim 1 .