Implant surface preparation
View Patent ↗The surface of a device that is surgically implantable in living bone is prepared. The device is made of titanium with a native oxide layer on the surface. The method of preparation comprises the steps of removing the native oxide layer from the surface of the device and performing further treatment of the surface substantially in the absence of unreacted oxygen.
1. A method of preparing the surface of an implant to be surgically implanted in living bone and made of titanium, the implant having a surface with a native oxide layer thereon, the method comprising the steps of:
removing the native oxide layer from the surface;
acid etching the surface from which the native oxide layer has been removed to form a substantially uniform surface roughness; and
depositing discrete particles of a bone-growth enhancing material on the acid-etched surface.
2. The method of claim 1 wherein the depositing occurs in an absence of oxygen.
3. The method of claim 1 wherein the depositing includes adhering, the adhering being enhanced by the roughness of the acid-etched surface.
4. The method of claim 1 wherein the bone-growth enhancing material includes hydroxyapatite.
5. The method of claim 4 wherein the hydroxyapatite depositing includes applying hydroxyapatite in the form of very small discrete particles.
6. The method of claim 1 wherein the depositing includes depositing the bone-growth enhancing material so as not to disturb the surface from which the native oxide layer has been removed.
7. The method of claim 1 wherein the acid-etching includes producing a substantially uniform surface roughness with a substantially uniform array of irregularities formed by a plurality of substantially cone-shaped elements.
8. The method of claim 7 wherein the depositing includes applying the bone-growth enhancing material in the form of fine particles located on the cone-shaped elements.
9. The method of claim 7 wherein the depositing includes applying the bone-growth enhancing material in the form of fine particles that become entrapped between the cone-shaped elements.
10. The method of claim 7 wherein the irregularities have peak-to-valley heights less than 10 microns.
11. The method of claim 1 wherein the depositing includes applying the bone-growth enhancing material using an inert atmosphere.
12. The method of claim 1 wherein the depositing includes distributing the bone-growth enhancing material, the distributing being enhanced by the substantially uniform surface roughness.
13. The method of claim 1 wherein the removing said native oxide layer is carried out by an acid etching process.
14. The method of claim 1 wherein the uniform surface roughness have peak-to-valley heights less than 10 microns.
15. A method of preparing a surface of a device that is surgically implantable in living bone, said device being made of titanium and having a native oxide layer on said surface, said method comprising the steps of:
removing the native oxide layer from the surface of the device until the depth of the peak-to-peak oxygen profile as measured by Auger spectrometer has decreased to one-half of the initial profile;
after the removing, performing a roughening treatment on the surface resulting from the removing to produce a roughened surface with a substantially uniform array of irregularities; and
after the performing a roughening treatment on the surface, depositing discrete particles of a bone-growth enhancing material on the surface.
16. The method of claim 15 wherein the performing a roughening treatment includes producing irregularities that include cone-shaped elements.
17. The method of claim 16 wherein the depositing includes applying the bone-growth enhancing material in the form of fine particles located on the cone-shaped elements.
18. The method of claim 16 wherein the depositing includes applying the bone-growth enhancing material in the form of fine particles located between the cone-shaped elements.
19. The method of claim 16 wherein the depositing includes applying the bone-growth enhancing material in the form of fine particles located on and between the cone-shaped elements.
20. The method of claim 15 wherein the performing the roughening treatment includes acid etching.
21. The method of claim 15 wherein the depositing occurs in the absence of oxygen.
22. The method of claim 15 wherein the depositing includes applying hydroxyapatite.
23. The method of claim 15 wherein the removing said native oxide layer is carried out by an acid etching process.
24. The method of claim 15 wherein the irregularities have peak-to-valley heights less than 10 microns.
25. A method of preparing the surface of an implant to be surgically implanted in living bone and made of titanium, the implant having a surface with a native oxide layer thereon, the method comprising the steps of:
removing the native oxide layer from the surface;
performing a roughening treatment on the surface to form a substantially uniform surface roughness with irregularities including cone-shaped elements; and
depositing discrete particles of hydroxyapatite on the roughened surface, the discrete particles being located on the cone-shaped elements.
26. The method of claim 25 , wherein the irregularities have peak-to-valley heights less than 10 microns.