Silica glass containing TiO
View Patent ↗A silica glass containing TiO 2 , which has a fictive temperature of at most 1,200° C., an OH group concentration of at most 600 ppm and a coefficient of thermal expansion of 0±200 ppb/° C. from 0 to 100° C.
1. A silica glass containing TiO 2 , which has a fictive temperature of at most 1100° C., an OH group concentration of at most 600 ppm and a coefficient of thermal expansion of 0±200 ppb/° C. from 0 to 100° C.
2. The silica glass containing TiO 2 according to claim 1 , which has an OH group concentration of at most 400 ppm.
3. The silica glass containing TiO 2 according to claim 1 , wherein the content of TiO 2 in the glass ranges from 1 to 12 mass %.
4. The silica glass containing TiO 2 according to claim 1 , wherein the fictive temperature is at most 1000° C.
5. The silica glass containing TiO 2 according to claim 1 , wherein the OH group concentration is at most 400 ppm.
6. A silica glass containing TiO 2 , which has a fictive temperature of at most 1,100° C., an OH group concentration of at most 600 ppm and a coefficient of thermal expansion of 0±200 ppb/° C. from −50 to 150° C.
7. The silica glass containing TiO 2 according to claim 6 , which has a fictive temperature of at most 850° C.
8. A TiO 2 —SiO 2 optical glass, comprising:
a silica glass having a fictive temperature of at most 1100° C., an OH group concentration of at most 600 ppm and a coefficient of thermal expansion of 0±200 ppb/° C. from 0 to 100° C., the distribution of the coefficient of thermal expansion throughout the silica glass being determined by fluctuations in the refractive index (Δn) which are determined by the difference between the maximum value and the minimum value of the refractive index determinations in at least one plane of the glass over an area of 30 mm×30 mm, is at most 2×10 −4 .