Spectroscopic monitoring of resin-application prior to assembly of composite wood veneer product
View Patent ↗Method for spectroscopically monitoring resin applied to a planar surface of veneer-wood sheets during travel in an assembly line. Spectroscopic instrumentation for monitoring applied resin is calibrated by measurements of predetermined resin applications to reference-test-samples, so as to provide a pre-determined relationship enabling monitoring of applied resin, during commercial production of a veneer-wood product using the visible light spectrum and near infrared extending to 2500 nm. Monitoring of selected radiation absorbance by the applied resin is carried out by spectroscopic measurement of non-absorbed electromagnetic radiation, as reflected back by the wood-veneer matrix; selected wavelengths are utilized for determining average resin-weight per designated surface area of a sheet. Selecting penetrative wavelengths enables use of multiple types of hardwood and softwood for veneer sheets during in-line production, providing for separate calibration for selected wood type and resin combinations measuring instrumentation.
1. Method for calibrating electromagnetic-radiation spectroscopic-instrumentation so as to enable quantitative analyses of curable resin, as applied to a substantially-planar veneer-wood sheet surface area during in-line movement of the sheet toward assembly of multiple-ply bundles for producing engineered-composite wood-veneer product, comprising
(A) providing spectroscopic-instrumentation enabling selecting wood-surface penetrative wavelengths of electromagnetic-radiation in a range of about 350 nm to about 2500 nm;
(B) quantitatively pre-establishing pre-determined surface-application of said resin, at a selected level of weight per specified surface area, for individual reference-source wood-veneer test-samples;
(C) supporting said test-samples with pre-established resin-application for movement on a conveyance;
(D) positioning spectroscopic instrumentation providing electromagnetic-radiation in a range of wavelengths including wavelengths absorbed by said resin and capable of penetrating wood-veneer of said test-samples;
(E) controlling rate of movement of said conveyed test-samples with respect to said instrumentation, and coordinating said rate of movement with a selected in-line controlled-rate of movement for lay-up of veneer-wood plies for commercial production of said engineered-composite veneer-wood product;
(F) illuminating a predetermined surface area of said pre-established resin application of said test-samples with visible light (VIS) and simultaneously irradiating with near infra-red (NIR), during said conveyed movement of said test samples relative to said instrumentation,
(G) quantitatively measuring radiation absorbance by pre-established resin applications to individual respective test-samples, for calibrating said spectroscopic-instrumentation, during said controlled rate of movement with respect to said instrumentation.
2. The invention of claim 1 , further including
(H) utilizing spectral-data responsive to absorbance of selected radiation wavelengths, by said pre-established resin-applications on said test-samples, for calibrating said spectroscopic instrumentation for monitoring resin-application, during commercial production of veneer-wood product, by verifying that a linear relationship exists between:
(i) spectroscopically determined absorbance of said selected wavelengths by applied resin, and
(ii) said quantitatively pre-established resin-application on respective individual test-samples.
3. The invention of claim 2 , including
(I) establishing resin-application on said test-samples so as to present an incrementally-progressive quantitative resin-application for veneer-wood of respective test-samples, with said quantitative resin-application being capable of being related to a resin-weight per specified surface area, during commercial production of a veneer-wood product;
(J) receiving spectral-data, in the form of non-absorbed radiant energy, of said selected wavelengths, as reflected back by said conveyed wood-veneer test samples, for spectroscopically determining absorbance of said selected wavelengths by said applied resin, and
(K) mathematically calculating radiation absorbance of resin applied to respective test samples, for establishing
(i) a linear-relationship between absorbance of said selected wavelengths, and
(ii) quantitative resin-application on said individual test-samples for calibrating said spectroscopic instrumentation for use during said commercial production.