Perpendicular magnetic recording medium with metamagnetic antiferromagnetically-coupled layer between the soft underlayer and recording layer
View Patent ↗A perpendicular magnetic recording medium includes a metamagnetic antiferromagnetically-coupled (AFC) layer between the recording layer (RL) and the soft magnetically permeable underlayer (SUL). The metamagnetic AFC layer has essentially no net magnetic moment in the absence of a magnetic field, but is highly ferromagnetic in the presence of a magnetic field above a threshold field. Thus the metamagnetic AFC layer does not contribute to the readback signal during reading, but channels the write field to the SUL during writing because the threshold field is selected to be below the write field. An exchange-break layer EBL is located between the metamagnetic AFC layer and the RL. The metamagnetic AFC layer contains films with a crystalline structure suitable as a growth template for the EBL and RL, so the metamagnetic AFC layer also functions as part of an “effective EBL”, thereby allowing the actual EBL to be made as thin as possible.
1. A perpendicular magnetic recording medium comprising:
a substrate;
an underlayer of magnetically permeable material on the substrate;
a perpendicular magnetic recording layer comprising a granular Co alloy having perpendicular magnetic anisotropy on the underlayer;
an antiferromagnetically-coupled (AFC) layer between the underlayer and the recording layer and having perpendicular magnetic anisotropy and substantially no net magnetic moment in the absence of an applied magnetic field, the AFC layer comprising a first multilayer of at least one pair of alternating first and second films, a second multilayer of at least one pair of alternating first and second films, and a nonmagnetic antiferromagnetically-coupling layer between the first and second multilayers, the first and second multilayers being perpendicularly antiferromagnetically exchange coupled across the antiferromagnetically-coupling layer and having perpendicular magnetizations substantially antiparallel in the absence of an applied magnetic field and substantially parallel in the presence of a magnetic field above a threshold field, the first film being Co or a Co alloy and the second film being selected from the group consisting of Pt, Pd, Au and Ni;
a nonmagnetic separation layer between the AFC layer and the underlayer; and
an exchange-break layer between the AFC layer and the recording layer for magnetically decoupling the recording layer and the AFC layer.
2. The medium of claim 1 wherein the Co alloy of the first film comprises Co and Fe.
3. The medium of claim 1 wherein the nonmagnetic antiferromagnetically-coupling layer of the AFC layer is formed of a material selected from the group consisting of ruthenium (Ru), chromium (Cr), rhodium (Rh), iridium (Ir), copper (Cu), and their alloys.
4. The medium of claim 1 wherein the AFC layer further comprises a third multilayer of alternating first and second films, and a nonmagnetic antiferromagnetically-coupling layer between the second multilayer and said third multilayer.
5. The medium of claim 1 wherein the exchange-break layer is a material selected from the group consisting of Ru, Ti, Re, Os, and an alloy of one or more of Ru, Ti, Re, and Os.
6. The medium of claim 1 wherein the exchange-break layer has a thickness less than approximately 80 Angstroms.
7. The medium of claim 1 wherein the combined thickness of the nonmagnetic separation layer, the AFC layer and the exchange-break layer is at least approximately 80 Angstroms.
8. The medium of claim 1 wherein the Co alloy of the recording layer comprises a CoPt alloy and wherein the recording layer further comprises an oxide or oxides of one or more of Si, Ti and Ta.
9. The medium of claim 1 wherein the recording layer is an antiferromagnetically-coupled (AFC) recording layer comprising first and second Co alloy layers having perpendicular magnetic anisotropy and separated by a nonmagnetic antiferromagnetically-coupling layer, the AFC recording layer having a substantial net magnetic moment in the absence of an applied magnetic field.
10. The medium of claim 1 wherein the underlayer is formed of a material selected from the group consisting of alloys of CoFe, CoNiFe, NiFe, FeCoB, CoCuFe, FeAlSi, FeTaN, FeN, FeTaC, CoTaZr and CoZrNb.
11. The medium of claim 1 wherein the underlayer is a lamination of multiple magnetically permeable films separated by nonmagnetic films.
12. The medium of claim 11 wherein the nonmagnetic films in the lamination provide antiferromagnetic coupling of the magnetically permeable films in the lamination.
13. A perpendicular magnetic recording disk comprising:
a substrate;
an underlayer of magnetically permeable material on the substrate;
a nonmagnetic separation layer on the underlayer;
a first multilayer on the separation layer and having perpendicular magnetic anisotropy, the first multilayer comprising alternating first and second films, the first film being Co or a Co alloy and the second film being selected from the group consisting of Pt, Pd, Au and Ni;
a second multilayer having perpendicular magnetic anisotropy and a magnetic moment substantially the same as the magnetic moment of the first multilayer in the absence of a magnetic field, the second multilayer comprising alternating first and second films, the first film being Co or a Co alloy and the second film being selected from the group consisting of Pt, Pd, Au and Ni;
a nonmagnetic antiferromagnetically-coupling layer between the first and second multilayers for perpendicularly antiferromagnetically coupling the first and second multilayers, the moments of the first and second multilayers being substantially antiparallel and thereby canceling one another in the absence of a magnetic field, the antiferromagnetically-coupling layer being a material selected from the group consisting of Ru, Cr, Rh, Ir, Cu, and their alloys;
a perpendicular magnetic recording layer comprising a granular Co alloy having perpendicular magnetic anisotropy; and
an exchange-break layer between the second multilayer and the recording layer for magnetically decoupling the recording layer and the second multilayer.
14. The disk of claim 13 wherein the first film of the first and second multilayers comprises a CoFe alloy.
15. The disk of claim 13 wherein the combined thickness of the nonmagnetic separation layer, the first and second multilayers, the antiferromagnetically-coupling layer and the exchange-break layer is at least approximately 80 Angstroms.
16. The disk of claim 13 wherein the exchange-break layer is a material selected from the group consisting of Ru, Ti, Re Os, and an alloy of one or more of Ru, Ti, Re, and Os.