Sugar additive blend useful as a binder or impregnant for carbon products
A sugar/additive blend useful as a binder or impregnant for carbon products. Simple sugars as well as sucrose are combined either in solution or in solid form with reactive additives such as ammonium hydrogen phosphate, ammonium chloride and para-toluene sulfuric acid. The sugar/additive blends form more and denser carbon residue than sugar alone when subjected to pyrolysis.
1 . A precursor composition for forming carbon or graphite artifacts, comprising a sugar and containing as an additive one or more reactive additives materials in an amount sufficient to accelerate the removal from the sugar of OH groups as water and the formation of double bonds in the sugar ring structure when exposed to heat, as compared to the sugar without the reactive additive present.
2 . The composition of claim 1 wherein the additive comprises an acid or acid salt.
3 . The composition of claim 2 wherein the additive is selected from the group consisting of a phosphate; ammonium chloride; zinc chloride; aluminum chlorate; or para-toluene sulfonic acid.
4 . The composition of claim 3 wherein the phosphate comprises ammonium dihydrogen phosphate and ammonium monohydrogen phosphate.
5 . The composition of claim 3 wherein the additive is present in an amount of up to about 6% by weight, based on the weight of the sugar.
6 . The composition of claim 1 wherein the the sugar and the the additive are dissolved in water to form an aqueous solution.
7 . A process for increasing the mechanical strength and decreasing the porosity of a carbonaceous material comprising the steps of (1) impregnating the carbonaceous material with a molten mixture of (a) a sugar and (b) one or more reactive additives sufficient to accelerate the removal of OH groups as water and the formation of double bonds in the sugar ring structure when heated, as compared to the sugar without the reactive additive present, and (2) baking the carbonaceous material for a time and at a temperature sufficient to convert at least about 75% of the carbon content of the sugar into a carbonaceous residue.
8 . The process of claim 7 wherein the reactive additive comprises an acid or acid salt.
9 . The process of claim 7 wherein the reactive additive is selected from the group consisting of a phosphate; ammonium chloride; zinc chloride; aluminum chlorate; or para-toluene sulfonic acid.
10 . The process of claim 9 wherein the phosphate comprises ammonium dihydrogen phosphate and ammonium monohydrogen phosphate.
11 . The process of claim 9 wherein the reactive additive is present in an amount of up to about 6% by weight, based on the weight of the sugar.
12 . The process of claim 7 wherein the sugar and the additive are dissolved in water to form an aqueous solution.
13 . A process for forming a carbonaceous material comprising the steps of (1) preparing a blend which comprises a carbon filler and a mixture of (a) a sugar and (b) one or more reactive additives sufficient to accelerate the removal of OH groups as water and the formation of double bonds in the sugar ring structure when heated, as compared to the sugar without the reactive additive present, and (2) baking the blend for a time and at a temperature sufficient to convert at least about 75% of the carbon content of the sugar into a carbonaceous residue.
14 . The process of claim 13 wherein the reactive additive comprises an acid or acid salt.
15 . The process of claim 14 wherein the reactive additive is selected from the group consisting of a phosphate; ammonium chloride; zinc chloride; aluminum chlorate; or para-toluene sulfonic acid.
16 . The process of claim 15 wherein the phosphate comprises ammonium dihydrogen phosphate and ammonium monohydrogen phosphate.
17 . The process of claim 13 wherein the reactive additive is present in an amount of up to about 6% by weight, based on the weight of the sugar.
18 . The process of claim 13 wherein the sugar and the reactive additive are dissolved in water to form an aqueous solution.
19 . The process of claim 13 wherein the carbon filler comprises coke.
20 . A carbonaceous product prepared by heating a carbonaceous source material together with a binder comprising (a) a sugar and (b) one or more reactive additives sufficient to accelerate the removal of OH groups as water and the formation of double bonds in the sugar ring structure when heated, as compared to the sugar without the reactive additive present, until the carbonaceous source material and binder are formed into an integral carbonaceous material, with at least about 75% of the initial intrinsic carbon content of the sugar being incorporated into the integral carbonaceous material.
21 . The product of claim 20 wherein the reactive additive comprises an acid or acid salt.
22 . The product of claim 21 wherein the reactive additive is selected from the group consisting of a phosphate; ammonium chloride; zinc chloride; aluminum chlorate; or para-toluene sulfonic acid.
23 . The product of claim 22 wherein the phosphate comprises ammonium dihydrogen phosphate and ammonium monohydrogen phosphate.
24 . The product of claim 20 wherein the reactive additive is present in an amount of up to about 6% by weight, based on the weight of the sugar.
25 . The product of claim 20 wherein the sugar and the reactive additive are dissolved in water to form an aqueous solution.