Method of anodizing valve metal derived anode bodies and electrolyte therefore
View Patent ↗An electrolyte solution for anodizing a metal and a capacitor comprising the anodized metal. The electrolyte comprises more than about 5%, by weight, and less than about 30%, by weight, water; about 0.1 to 20%, by weight, ionogen and an aprotic polar solvent. The ionogen comprises phosphoric acid and an alkanol amine in an amount, and ratio, sufficient to maintain a pH of about 4 to about 9.
1. An anode anodized by the electrolyte comprising:
more than about 5%, by weight, and less than about 30%, by weight, water; about 0.1 to 20%, by weight, ionogen comprising:
phosphoric acid; and
an alkanol amine wherein the amount of ionogen is sufficient to maintain a pH of about 4 to about 9; and
an aprotic polar solvent.
2. An anode of claim 1 comprising a valve metal selected from titanium, tungsten, chromium, aluminium, zirconium, hafnium, zinc, vanadium, niobium, tantalum, bismuth, antimony and mixtures, alloys and metallic glass compositions thereof.
3. The anode of claim 2 wherein saidanode comprises tantalum.
4. A capacitor comprising the anode of claim 3 .
5. An anode anodized by the method of:
providing a valve metal;
placing said valve metal in an electrolyte comprising:
more than about 5%, by weight, and less than about 30%, by weight, water;
about 0.1 to 20%, by weight, ionogen comprising:
phosphoric acid; and
an alkanol amine wherein the amount of ionogen is sufficient to maintain a pH of about 4 to about 9; and
an aprotic polar solvent; and
subjecting said valve metal to an anodizing voltage.
6. The anode of claim 5 , wherein said valve metal is selected from titanium, tungsten, chromium, aluminium, zirconium, hafnium, zinc, vanadium, niobium, tantalum, bismuth, antimony and mixtures, alloys and metallic glass compositions thereof.
7. The anode of claim 6 , wherein said valve metal comprises tantalum.
8. A capacitor comprising the anode of claim 7 .
9. A capacitor formed by the process of:
providing a valve metal;
placing said valve metal in an electrolyte comprising:
more than about 5%, by weight, and less than about 30%, by weight, water;
about 0.1 to 20%, by weight, ionogen comprising:
phosphoric acid; and
an alkanol amine wherein the amount of ionogen is sufficient to maintain a pH of about 4 to about 9; and
an aprotic polar solvent; and
subjecting said valve metal to an anodizing voltage to form an anodized anode;
forming a capacitor with said anodized anode.
10. The capacitor of claim 9 wherein said alkanol amine is selected from monoethanol amine, diethanol amine, triethanol amine, ethyl diethanolamine, diethyl ethanolamine, dimethyl ethanolamine and dimethyl ethoxy ethanolamine.
11. The capacitor of claim 10 wherein said alkanol amine is selected from dimethyl ethanolamine and dimethyl ethoxy ethanolamine.
12. The capacitor of claim 9 wherein said aprotic polar solvent comprises an N-alkyl amide.
13. The capacitor of claim 12 wherein said N-alkyl amide is selected from dimethyl formamide and dimethyl acetamide.
14. The capacitor of claim 13 wherein said aprotic polar solvent comprises dimethyl sulfoxide.
15. The capacitor of claim 9 wherein said electrolyte comprises about 0.1 to about 15%, by weight, ionogen.
16. The capacitor of claim 15 wherein said electrolyte comprises about 0.5 to about 5%, by weight, phosphoric acid.
17. The capacitor of claim 15 wherein said electrolyte comprises about 0.5 to about 7%, by weight, said alkanol amine.
18. The capacitor of claim 9 wherein said valve metal is selected from titanium, tungsten, chromium, aluminium, zirconium, hafnium, zinc, vanadium, niobium, tantalum, bismuth, antimony and mixtures, alloys and metallic glasses thereof.
19. The capacitor of claim 18 wherein said valve metal comprises tantalum.