Rolling bearing of ceramic and steel engaging parts
View Patent ↗A roller bearing having two cooperating rolling parts of which one is of ceramic and the other of a steel. The steel part is of such structure and/or material and/or is so produced to cause residual compressive stresses to form beneath the contact surface of the steel part, at least in a load-free state, down to a depth.
1. A roller bearing comprising:
at least one first rolling part of a ceramic material having a first contact surface;
at least one second cooperating rolling part comprising steel with a martensitic microstructure and having a second contact surface, at least a portion of the second contact surface configured and positioned to make rolling contact with the first surface; and
the microstructure having residual compressive stresses beneath at least a portion of the second contact surface at least in a load-free state,
wherein a level of the residual compressive stresses of an entire region starting from the second surface down to a depth of 40 μm corresponds at least to an absolute value of 300 MPa, wherein the residual stresses decrease in magnitude below the depth of 40 μm, and
wherein the second rolling part includes a thermochemically produced outer layer to include the second contact surface, and the second contact surface is fully machined, wherein the thermochemically produced outer layer is nitrogen-enriched, wherein the outer layer of the second rolling part, at least at the second surface, has a hardness of at least 850 HV0.3 at a depth of 0.05 mm below the second surface, wherein the outer layer has been heat-treated twice, and the second heat treatment is at a process temperature of at least 400° C.
2. The roller bearing as claimed in claim 1 , wherein the thermochemically produced outer layer is produced by plasma nitriding.
3. The roller bearing as claimed in claim 1 , wherein the second rolling part comprises steel of designation M50, comprising:
0.8 to 0.85% by weight of carbon,
4 to 4.25% by weight of chromium,
4 to 4.5% by weight of molybdenum,
0.9 to 1.1% by weight of vanadium,
0.15 to 0.35% by weight of manganese,
0.1 to 0.25% by weight of silicon,
maximum 0.015% by weight of phosphorus, and
maximum 0.008% by weight of sulfur.
4. The roller bearing as claimed in claim 1 , wherein the second rolling part comprises steel of designation M50NiL, comprising:
0.11 to 0.15% by weight of carbon,
4.0 to 4.25% by weight of chromium,
4.0 to 4.5% by weight of molybdenum,
1.1 to 1.3% by weight of vanadium,
3.2 to 3.6% by weight of nickel,
0.15 to 0.35% by weight of manganese,
0.1 to 0.25% by weight of silicon,
maximum 0.015% by weight of phosphorus, and
maximum 0.008% by weight of sulfur.
5. The roller bearing as claimed in claim 1 , wherein the second rolling part comprises steel of designation 32CD V13, comprising:
0.29 to 0.36% by weight of carbon,
2.8 to 3.3% by weight of chromium,
0.7 to 1.2% by weight of molybdenum,
0.15 to 0.35% by weight of vanadium,
0.4 to 0.7% by weight of manganese,
0.1 to 0.4% by weight of silicon,
maximum 0.025% by weight of phosphorus, and
maximum 0.02% by weight of sulfur.
6. The roller bearing as claimed in claim 1 , wherein the second rolling part comprises steel of designation T1 (S 18-0-1), comprising:
0.7 to 0.8% by weight of carbon,
4 to 5% by weight of chromium,
17.5 to 18.5% by weight of tungsten,
1 to 1.5% by weight of vanadium,
0 to 0.4% by weight of manganese,
0.15 to 0.35% by weight of silicon,
maximum 0.025% by weight of phosphorus, and
maximum 0.008% by weight of sulfur.
7. The roller bearing as claimed in claim 1 , wherein the second rolling part comprises steel of designation RBD, comprising:
0.17 to 0.21% by weight of carbon,
2.75 to 3.25% by weight of chromium,
9.5 to 10.5% by weight of tungsten,
0.2 to 0.4% by weight of manganese,
0 to 0.35% by weight of silicon,
0.35 to 0.5% by weight of vanadium,
maximum 0.015% by weight of phosphorus, and
maximum 0.015% by weight of sulfur.
8. The roller bearing as claimed in claim 1 , wherein the second rolling part comprises steel comprising:
0.06 to 0.08% by weight of carbon,
12.8 to 13.3% by weight of chromium,
1.5 to 2.0% by weight of molybdenum,
0.5 to 0.7% by weight of vanadium,
2.2 to 2.8% by weight of nickel,
4.8 to 5.8% by weight of cobalt,
0.5 to 1.0% by weight of manganese, and
0.2 to 0.6% by weight of silicon.
9. The roller bearing as claimed in claim 1 , wherein the first rolling part comprises silicon nitride.
10. The roller bearing as claimed in claim 1 , wherein the second rolling part is a bearing ring.
11. The roller bearing as claimed in claim 1 , wherein the second rolling part is at least one rolling body.