Interlayers comprising an ultraviolet curable layer
The present invention is in the field of interlayers for use in multiple layer glass panels, and more specifically, the present invention is in the field of multiple layer glass panel interlayers comprising an ultraviolet curable layer.
1 . A polymer interlayer comprising:
a polymer stack comprising a first polymer sheet, wherein said first polymer sheet comprises a thermoplastic polymer; and,
a second polymer sheet, wherein said second polymer sheet comprises an ultraviolet curable polymer and is disposed in contact with said first polymer sheet.
2 . The polymer interlayer of claim 1 , wherein said first polymer sheet comprises poly(vinyl butyral).
3 . The polymer interlayer of claim 1 , wherein said second polymer sheet comprises an ultraviolet curable polymer selected from the group consisting of methyl methacrylate, ethyl methacrylate, methacrylic acid, 2-ethylhexyl acrylate, acrylic acid, isobomyl methacrylate, ethylene glycol dimethacrylate, tetraethylene glycol dimethacrylate, diethylene glycol dimethacrylate, urethane acrylate, polyester acrylate, epoxy acrylate, full acrylics, amino acrylate, vinyl ether, and combinations of the foregoing.
4 . The polymer interlayer of claim 1 , wherein said second polymer sheet comprises an ultraviolet curable polymer selected from the group consisting of urethane acrylate, ethylhexyl acrylate, acrylic acid, and combinations of the foregoing.
5 . The polymer interlayer of claim 1 , wherein said second polymer sheet is disposed in contact with said second polymer sheet.
6 . The polymer interlayer of claim 1 , wherein said polymer stack further comprises a polymer film.
7 . The polymer interlayer of claim 1 , wherein the glass transition temperature of said second polymer sheet is less than 80° C. and the glass transition temperature of said first polymer sheet is at least 20° C.
8 . The polymer interlayer of claim 1 , wherein the glass transition temperature of said second polymer sheet is less than 20° C. and the glass transition temperature of said first polymer sheet is at least 20° C.
9 . The polymer interlayer of claim 1 , further comprising a second polymer stack disposed in contact with said second polymer sheet, wherein said second polymer stack comprises a third polymer sheet comprising a plasticized thermoplastic polymer.
10 . The polymer interlayer of claim 9 , wherein said third polymer sheet comprises poly(vinyl butyral) and has a glass transition temperature above 20° C.
11 . The polymer interlayer of claim 10 , wherein said third polymer sheet is disposed in contact with said second polymer sheet.
12 . A method for manufacturing an interlayer, comprising:
providing a first polymer sheet;
forming a layer of ultraviolet curable resin on said first polymer sheet; and,
curing said layer of ultraviolet curable resin to form a second polymer sheet.
13 . The method of claim 12 , wherein said first polymer sheet comprises poly(vinyl butyral).
14 . The method of claim 13 , wherein said ultraviolet curable polymer is selected from the group consisting of methyl methacrylate, ethyl methacrylate, methacrylic acid, 2-ethylhexyl acrylate, acrylic acid, isobomyl methacrylate, ethylene glycol dimethacrylate, tetraethylene glycol dimethacrylate, diethylene glycol dimethacrylate, urethane acrylate, polyester acrylate, epoxy acrylate, full acrylic, amino acrylate, vinyl ether, and combinations of the foregoing.
15 . The method of claim 13 , wherein said ultraviolet curable polymer is selected from the group consisting of urethane acrylate, ethylhexyl acrylate, acrylic acid, and combinations of the foregoing.
16 . The method of claim 12 , wherein said forming comprises applying ultraviolet curable reason on said first polymer sheet by slot die coating, knife and blade coating, spray coating, or gravure coating.
17 . The method of claim 12 , wherein said forming comprises knife and blade coating or slot die coating.
18 . The method of claim 12 , further comprising disposing a third polymer sheet in contact with said second polymer sheet and laminating said first polymer sheet, said second polymer sheet, and said third polymer sheet.
19 . The method of claim 12 , further comprising disposing a polymer film in contact with said second polymer sheet, disposing a third polymer sheet in contact with said polymer film, and laminating said first polymer sheet, said second polymer sheet, said polymer film, and said third polymer sheet.
20 . The method of claim 12 , wherein the glass transition temperature of said second polymer sheet is less than 80° C. and the glass transition temperature of said first polymer sheet is at least 20° C.