Cerium-based abrasive and production process thereof
View Patent ↗A mixed light rare earth compound which has been obtained by chemically removing medium-to-heavy rare earth elements, Nd and impurities other than rare earth elements from an ore containing rare earth elements is fired at 500 to 1100° C. to yield a mixed rare earth oxide. A cerium-based rare earth oxy-fluoride is added to the mixed rare earth oxide to obtain a mixture. The mixture is subjected to wet-pulverization, drying, firing, disintegration and classification to thereby yield a cerium-containing abrasive.
1. A process for producing a cerium-containing abrasive comprising cubic composite rare earth oxide and composite rare earth oxy-fluoride, wherein the cerium-containing abrasive contains not less than 90 mass % of rare earth elements in terms of oxide and the rare earth elements contain not less than 55 mass % of cerium in terms of oxide, comprising firing at 500 to 1100° C. a mixed light rare earth compound which has been obtained by chemically removing medium-to-heavy rare earth elements, Nd and impurities other than rare earth elements from an ore containing rare earth elements to thereby yield a mixed rare earth oxide, and adding a cerium-based rare earth fluoride to the mixed rare earth oxide to obtain an abrasive that contains not less than 90 mass % of rare earth elements in terms of oxide and the rare earth elements contain not less than 55 mass % of cerium in terms of oxide.
2. The producing process according to claim 1 , further comprising, after adding the cerium-based rare earth fluoride to the mixed rare earth oxide to obtain a mixture, subjecting the mixture to wet-pulverization, drying, firing, disintegration and classification to thereby yield a cerium-containing abrasive.
3. The producing process according to claim 1 , further comprising, adding mixed rare earth carbonate obtained by carbonating the mixed light rare earth compound to the mixed rare earth oxide and cerium-based rare earth fluoride to obtain a mixture and subjecting the mixture to wet-pulverization, drying, firing, disintegration and classification to thereby yield a cerium-containing abrasive.
4. The producing process according to claim 2 , wherein the rare earth fluoride is fluoride of a cerium-based mixed light rare earth compound that is obtained by adding fluoride to the mixed light rare earth compound and heat-treating the resultant mixture at a temperature of not more than 400° C.
5. The producing process according to any one of claims 1 to 4 , wherein the firing is performed in an atmosphere for 2 to 36 hours in a firing furnace.
6. The producing process according to claim 5 , wherein the firing furnace is an electrical furnace or a pusher furnace.
7. The producing process according to claim 1 , wherein the abrasive contains 5 to 10 mass % fluorine.