Low dielectric composite materials including high modulus polyolefin fibers
View Patent ↗Disclosed are composite laminates that can exhibit high strength and/or low dielectric loss and can also be lightweight. The laminates include layers formed of high modulus polyolefin fiber. The fibers can be woven or knit to form a fabric or can be included in a nonwoven fabric that can be one or more layers of the composite structures. The layers including the high modulus polyolefin fibers can include other fibers, such as fiberglass. The composites can also include layers of other materials, for instance layers formed of polyaramids, fiberglass, or carbon fiber wovens or nonwovens. The composites can advantageously be utilized in low loss dielectric applications, such as in forming circuit board substrates, or in applications beneficially combining strength with low weight, such as automobile and boat materials.
1. A method comprising:
i) providing an electromagnetic wave at a frequency between about 100 kHz and about 100 GHz;
ii) placing a laminate structure in the path of the electromagnetic wave, the laminate structure comprising a fabric layer comprising a plurality of semi-crystalline multi-filament polypropylene fibers having a modulus greater than about 8 GPa and exhibiting at least one of the following characteristics: a) a tenacity greater than 400 MPa, b) greater than 80% crystallinity according to WAXS measuring techniques, and c) a ratio of equatorial intensity to meridonal intensity of greater than 1.0 as measured by SAXS techniques, wherein the laminate structure is essentially transparent to electromagnetic energy and exhibits a dielectric constant of less than about 3.5; wherein said polypropylene fibers alone exhibit a dielectric constant of less than about 3.5, and wherein said polypropylene fibers further exhibit a capability to impart a flexural strength of at least 80 MPa to a laminate structure of eight fabric layers consisting of said polypropylene fibers as the only fibers present; and
iii) passing the electromagnetic wave through the laminate structure.
2. The method of claim 1 , wherein the electromagnetic wave is transmitted from a dish antenna.
3. The method of claim 1 , wherein the laminate structure is a portion of a protective enclosure housing an electromagnetic wave transmitter, and electromagnetic wave receiver, or both.
4. The method of claim 1 , wherein the fabric layer comprising the polypropylene fibers is an inner layer of the laminate structure, the laminate structure further comprising an external layer comprising fibers selected from the group consisting of glass fibers, polyaramid fibers, and ultra-high molecular weight polyethylene fibers.
5. The method of claim 4 , in which the external layer is a fiberglass fabric.
6. The method of claim 1 , further comprising reflecting the electromagnetic wave off of an object, and subsequently passing the electromagnetic wave through the laminate structure a second time.
7. The method of claim 6 , wherein the object is a cloud.
8. The method of claim 6 , wherein the object is a vehicle.
9. The method of claim 8 , wherein the object is an aircraft.
10. The method of claim 1 , wherein the fabric layer is a weave fabric comprising the polypropylene fibers in an interlaced pattern with a plurality of second fibers.
11. The method of claim 1 , in which the laminate structure comprises a low loss thermoset resin.
12. A method comprising:
i) providing an electromagnetic wave at a frequency between about 100 kHz and about 100 GHz;
ii) placing a laminate structure in the path of the electromagnetic wave, the laminate structure comprising a fabric layer comprising a plurality of semi-crystalline multi-filament polypropylene fibers having a modulus greater than about 8 GPa and a maximum cross sectional dimension less than about 100 microns;
wherein the laminate structure is essentially transparent to electromagnetic energy and exhibits a dielectric constant of less than about 3.5;
wherein said polypropylene fibers alone exhibit a dielectric constant of less than about 3.5; and
wherein said laminate structure has an average density less than about 1.5 g/cm 3 , a flexural strength greater than about 100 MPa, and a flexural modulus greater than about 10 GPa; and
iii) passing the electromagnetic wave through the laminate structure.