Non-heat treated connecting rod and method of manufacturing the same
View Patent ↗A non-heat treated connecting rod which comprises, by mass %, C: 0.25-0.35%, Si: 0.50-0.70%, Mn: 0.60-0.90%, P: 0.040-0.070%, S: 0.040-0.130%, Cr: 0.10-0.20%, V: 0.15-0.20%, Ti: 0.15-0.20% and N: 0.002-0.020%, and the balance Fe and impurities, with chemical compositions being less than 0.80 in the value of C+(Si/10)+(Mn/5)+(5Cr/22)+1.65 V−(5S/7) using the symbol of the element as its content, the microstructure of the Big end of the said connecting rod being ferrite-pearlite, all-region hardness of the said big end being 255 to 320 in Vickers hardness, the ferrite-region hardness in the said ferrite-pearlite of the Big end being 250 or more in Vickers hardness and the ratio of the said ferrite-region hardness to the said all-region hardness of the said Big end being 0.80 or more, is excellent in machinability, fracture splitting ability, and fatigue resistance, although no Pb at all is added. Therefore, this non-heat treated connecting rod can be utilized as a low cost type connecting rod in automobile engines or the like.
1. A non-heat treated fracture splitting connecting rod which comprises, in % by mass, C: 0.25 to 0.35%, Si: 0.50 to 0.70%, Mn: 0.60 to 0.90%, P: 0.040 to 0.070 %, S: 0.040 to 0.130%, Cr: 0.10 to 0.20%, V: 0.15 to 0.20%, Ti: 0.15 to 0.20% and N: 0.002 to 0.020%, with the balance being Fe and impurities, with chemical compositions being less than 0.80 in the value of Ceq stated by the following expression (1), the microstructure of the big end of the said connecting rod being ferrite-pearlite, all-region hardness of the said big end being 255 to 320 in Vickers hardness, the ferrite-region hardness in the said ferrite-pearlite of the big end being 250 or more in Vickers hardness and the ratio of the said ferrite-region hardness to the said all-region hardness of said big end being 0.80 or more;
C eq =C+(Si/10)+(Mn/5)+(5Cr/22)+1.65V−(5S/7) (1),
where an element symbol appearing in the expression (1) represents the contents in mass % of the corresponding elements in the steel.
2. A method of manufacturing a non-heat treated connecting rod which comprises, in % by mass, C: 0.25 to 0.35%, Si: 0.50 to 0.70 %, Mn: 0.60 to 0.90%, P: 0.040 to 0.070%, S: 0.040 to 0.130%, Cr: 0.10 to 0.20%, V: 0. 15 to 0.20%, Ti: 0.15 to 0.20% and N: 0.002 to 0.020 %, with the balance being Fe and impurities, with chemical compositions being less than 0.80 in the value of Ceq stated by the following expression (1), the microstructure of the big end of the said connecting rod being ferrite-pearlite, all-region hardness of the said big end being 255 to 320 in Vickers hardness, the ferrite-region hardness In the said ferrite-pearlite of the Big end being 250 or more in Vickers hardness and the ratio of the said ferrite-region hardness to the said all-region hardness of the said big end being 0.80 or more, the said method sequentially comprising the following steps (a) to (f):
(a) heating a steel having the said chemical compositions at 1200 to 1350° C.;
(b) hot forging a connecting rod body and a connecting rod cap at 900° C. or more into an integral forged material;
(c) hot coining of the big end at a temperature of more than 800° C.;
(d) providing a notch on the big end;
(e) fracture splitting into a connecting rod body and a connecting rod cap from a portion where the said notch on the big end was provided;
(f) assembling the said fracture split connecting rod body and the connecting rod cap;
C eq =C+(Si/10)+(Mn/5)+(5Cr/22)+1.65V−(5S/7) (1),
where an element symbol appearing in the expression (1) represents the contents in mass % of the corresponding elements in the steel.