Polyester polymer and copolymer compositions containing particles of titanium nitride and carbon-coated iron
View Patent ↗Polyester compositions are disclosed that include polyester polymers or copolymers having incorporated therein titanium nitride particles and carbon-coated iron particles to improve the reheat properties of the compositions. The compositions may also exhibit reduced yellowness, and improved resistance to the effects of UV light. Processes for making such compositions are also disclosed. The particles may be incorporated in the polyester by melt compounding, or may be added at any stage of the polymerization, such as during the melt-phase of the polymerization. A range of particle sizes may be used, as well as a range of particle size distributions. The polyester compositions are suitable for use in packaging made from processes in which a reheat step is desirable, or decreased yellowness is desired, or increased resistance to the effects of ultraviolet light is desired, or any combination of the foregoing.
1. A polyester composition comprising:
a polyester polymer;
carbon-coated metal iron particles, having a median particle size from 1 nm to about 1,000 nm, dispersed in the polyester polymer, wherein the carbon-coated metal iron particles comprise an iron core in which iron is present in an amount of at least 50 wt. %, with respect to the total weight of the iron core; and
titanium nitride particles, having a median particle size of from about 1 nm to about 1,000 nm, dispersed in the polyester polymer,
wherein the polyester composition is in the form of a beverage bottle preform or a beverage bottle.
2. The polyester composition of claim 1 , wherein both the titanium nitride particles and the carbon-coated metal iron particles have a median particle size from about 1 nm to about 500 nm.
3. The polyester composition of claim 1 , wherein both the titanium nitride particles and the carbon-coated metal iron particles have a median particle size from about 1 nm to about 300 nm.
4. The polyester composition of claim 1 , wherein the total amount of the titanium nitride particles and the carbon-coated metal iron particles is from about 0.5 ppm to 1,000 ppm, with respect to the total weight of the polyester composition.
5. The polyester composition of claim 1 , wherein the total amount of the titanium nitride particles and the carbon-coated metal iron particles is from 1 ppm to 500 ppm, with respect to the total weight of the polyester composition.
6. The polyester composition of claim 1 , wherein the titanium nitride particles are present in an amount of from 5 ppm to 50 ppm, with respect to the total weight of the polyester composition.
7. The polyester composition of claim 1 , wherein the polyester polymer comprises polyethylene terephthalate.
8. The polyester composition of claim 1 , wherein the polyester polymer comprises a continuous phase, and wherein the titanium nitride and the carbon-coated metal iron particles are dispersed within the continuous phase.
9. The polyester composition of claim 1 , wherein the titanium nitride particles and the carbon-coated metal iron particles have a median particle size from 1 nm to 1,000 nm, and provide the beverage bottle preform with a reheat improvement temperature (RIT) of at least 5° C. while maintaining a preform L* value of 70 or more, and a b* value from about minus 0.8 to about plus 2.5.
10. The polyester composition of claim 1 , wherein the titanium nitride particles comprise particles coated with titanium nitride.
11. The polyester composition of claim 1 , wherein the titanium nitride particles comprise hollow spheres comprised of titanium nitride.
12. The polyester composition of claim 1 , wherein the titanium nitride particles comprise a titanium nitride having an empirical formula from about TiN 0.42 to about TiN 1.16 .
13. The polyester composition of claim 1 , wherein the titanium nitride particles comprise titanium nitride in an amount of at least about 90 wt.%, with respect to the total weight of the titanium nitride particles.
14. The polyester composition of claim 13 , wherein the titanium nitride particles further comprise titanium carbide.
15. The polyester composition of claim 1 , wherein the titanium nitride particles have a particle size distribution in which the span (S) is from 0.01 to 2.
16. The polyester composition of claim 1 , wherein the polyester composition is in the form of a beverage bottle preform having a reheat improvement temperature greater than 5° C.
17. The polyester composition of claim 1 , wherein the polyester composition is in the form of a beverage bottle preform having a b* value from about −8.6 to about 10.2.
18. The polyester composition of claim 1 , wherein the polyester composition is in the form of a beverage bottle preform having a b* value that is at least 1 unit less than it would be in the absence of the titanium nitride particles.
19. The polyester composition of claim 1 , wherein the polyester composition is in the form of a beverage bottle in which the percent transmission rate at 370 nm is from about 78% to about 0%.
20. The polyester composition of claim 1 , wherein the polyester composition is in the form of a beverage bottle preform in which the percent transmission rate at 370 nm is from about 78% to about 20%.
21. The polyester composition of claim 1 , wherein the polyester composition is in the form of a beverage bottle preform in which the percent transmission rate at 370 nm is at least 20 percent less than it would be in the absence of the titanium nitride particles.
22. The polyester composition of claim 1 , wherein the polyester composition is in the form of a beverage bottle preform in which the percent transmission rate at 370 nm is at least 5 percent less than it would be in the absence of the titanium nitride particles.
23. A polyester composition comprising:
a polyester polymer in which poly(ethylene terephthalate) residues comprise at least 90 wt. % of the polyester polymer;
carbon-coated metal iron particles, having a median particle size from 1 nm to about 1,000 nm, randomly dispersed in the polyester polymer in an amount from about 1 to about 50 ppm, wherein the carbon-coated metal iron particles comprise an iron core in which iron is present in an amount of at least 50 wt. %, with respect to the total weight of the iron core; and
titanium nitride particles, having a median particle size of from about 1 nm to about 1,000 nm, randomly dispersed in the polyester polymer in an amount of from 1 to about 50 ppm, wherein the polyester composition is in the form of a beverage bottle preform or a beverage bottle preform having a reheat improvement temperature of 5° C. or more, and a b* value that is at least 1 unit less than it would be in the absence of the titanium nitride particles.