Poly(arylene ether) composition, method, and article
View Patent ↗A synergistic flame retardant combination includes (a) a phosphorus salt having the formula wherein M d+ is a metal ion or an onium ion; d is 1, 2, 3, or 4 according to the identity of M and its oxidation state; each occurrence of R 1 and R 2 is independently C 1 -C 18 hydrocarbyl; and each occurrence of m and n is independently 0 or 1; and (b) a phosphine compound selected from trihydrocarbylphosphines, trihydrocarbylphosphine oxides, and combinations thereof. Polymer compositions utilizing the flame retardant combination are described.
1. A curable composition, comprising:
(a) a capped functionalized poly(arylene ether) resin;
(b) a curable compound selected from triallyl cyanurate, triallyl isocyanurate, bismaleimide resins, bismaleimide triazine resins, and combinations thereof; and
(c) a flame retardant, comprising
a phosphorus salt having the formula
wherein M d+ is Al 3+ ; d is 3; each occurrence of R 1 and R 2 is independently C 1 -C 6 hydrocarbyl; and each occurrence of m and n is independently 0; and
a trihydrocarbylphosphine oxide having the structure
wherein R 3 -R 5 are each independently C 3 -C 12 hydrocarbyl;
wherein the phosphorus salt is present in the amount of 20 to 80 parts by weight and the trihydrocarbylphosphine oxide is present in the amount of 80 to 20 parts by weight, based on 100 parts by weight total of the phosphorus salt and the trihydrocarbylphosphine oxide, and wherein the curable composition comprises about 1 to about 40 parts by weight of the flame retardant, based on 100 parts by weight total of the functionalized capped poly(arylene ether) resin, the curable compound, and the flame retardant.
2. A curable composition, comprising:
(a) a functionalized poly(arylene ether) resin that comprises a (meth)acrylate-capped poly(2,6-dimethyl-1,4-phenylene ether) resin;
(b) a curable compound that comprises a triallyl cyanurate, a triallyl isocyanurate, or a combination thereof; and
(c) flame retardant compounds comprising aluminum tris(diethylphosphinate) and a phosphine oxide selected from triphenylphosphine oxide, allyldiphenylphosphine oxide, diallylphenylphosphine oxide, triallylphosphine oxide, and combinations thereof;
wherein the phosphorus salt is present in the amount of 20 to 80 parts by weight and the phosphine oxide is present in the amount of 80 to 20 parts by weight, based on 100 parts by weight total of the phosphorus salt and the phosphine oxide, and wherein the curable composition comprises about 1 to about 40 parts by weight of the flame retardant compounds, based on 100 parts by weight total of the functionalized poly(arylene ether) resin, the curable compound, and the flame retardant compounds.
3. A cured composition, comprising the cured product of the curable composition of claim 1 .
4. An article comprising the composition of claim 3 .
5. A method of preparing a curable composition, comprising:
blending
(a) a functionalized poly(arylene ether) resin;
(b) a curable compound selected from triallyl cyanurate, triallyl isocyanurate, epoxy resins, bismaleimide resins, bismaleimide triazine resins, and combinations thereof; and
(c) a flame retardant, comprising
(c1) a phosphorus salt having the formula
wherein M d+ is Al 3+ ; d is each occurrence of R 1 and R 2 independently C 1 -C 6 hydrocarbyl; and each occurrence of m and n is independently 0; and
(c2) a trihydrocarbylphosphine oxide having the structure
wherein R 3 -R 5 are each independently C 3 -C 12 hydrocarbyl; to form an intimate blend;
wherein the phosphorus salt is present in the amount of 20 to 80 parts by weight and the trihydrocarbylphosphine oxide is present in the amount of 80 to 20 parts by weight, based on 100 parts by weight total of the phosphorus salt and the trihydrocarbylphosphine oxide and wherein the curable composition comprises about 1 to about 40 parts by weight of the flame retardant, based on 100 parts by weight total of the functionalized poly(arylene ether) resin, the curable compound, and the flame retardant.