Alignment of paste-like ink having magnetic particles therein, and the printing of optical effects
View Patent ↗A method and apparatus is provided for printing using paste like inks such as those used in intaglio printing, wherein the inks include specialty flakes such as thin film optically variable flakes, or diffractive flakes. The invention discloses an apparatus having an energy source such as a heat source for temporarily lessening the viscosity of the ink during alignment of the flakes within the ink.
1. A method of forming an image on a substrate, the image providing an optical effect caused by an alignment of flakes within the image, the method comprising the steps of:
a) printing a viscous paste ink onto the substrate, the viscous paste ink comprising a carrier having flakes therein, wherein the flakes are optical interference pigment flakes, or reflective pigment flakes, or single layer diffractive flakes, or multi layer diffractive flakes, and wherein the flakes comprise at least a layer of field orientable material;
b) after step (a), lessening the viscosity of the paste ink by adding energy to the paste ink printed on the substrate, wherein a configuration of the paste ink printed on the substrate is maintained;
c) after the viscosity of the paste ink is lessened, applying a magnetic or electric field so as to reorient the flakes within the paste ink and to provide the alignment of the flakes such that some of the flakes are standing on their edges or tilted thereby enabling the optical effect; and,
d) fixing the alignment of the flakes within the paste ink on the substrate; wherein the paste ink remains a paste during steps (a)-(c).
2. A method as defined in claim 1 , wherein the paste ink has a viscosity V of at least 100 Pa·s when at a temperature of between 15 and 25 degrees C.
3. A method as defined in claim 1 , wherein the step of lessening the viscosity includes decreasing the viscosity V of the paste ink by at least 60% for at least a time sufficient for applying the magnetic or electric field to the paste ink, so as to allow the flakes to align within the paste ink along field lines of the magnetic or electric field.
4. A method as defined in claim 1 , wherein in step (b) the viscosity V is decreased by at least 80%.
5. A method as defined in claim 1 , wherein the step of lessening the viscosity V of the paste ink comprises the step of heating the paste ink after step (a).
6. A method as defined in claim 5 , wherein the step of heating the paste ink is performed by heating the substrate.
7. A method as defined in claim 5 , wherein the ink is printed on the substrate using a printing roller and an impression roller and wherein the step of heating is performed by applying heat downstream from the printing roller.
8. A method as defined in claim 5 , wherein the step of heating includes passing the substrate along a heated element.
9. A method as defined in claim 1 , wherein the viscosity of the paste ink is lessened after printing the paste ink on the substrate, proximate to where the printing occurs.
10. A method as defined in claim 1 wherein the step of fixing includes curing the paste ink after the magnetic flakes have been aligned in step (c).
11. A method as defined in claim 10 , wherein the curing step involves a first portion of less than 5 minutes in which surface drying occurs followed by a second portion in which a sub-surface cures.
12. A method as defined in claim 10 , wherein the step of curing includes irradiation the ink with UV light or ebeam right after a heating of the ink.
13. A method as defined in claim 10 , wherein the step of curing includes the step of irradiating the ink with UV light.
14. A method as defined in claim 10 , wherein the step of curing includes the step of irradiating the ink with an electron beam.
15. A method as defined in claim 1 , wherein the paste ink includes slow drying solvents and/or a cure retarder.