Curable silicone release composition and sheet having a releasability using the same
View Patent ↗A curable silicone composition which comprises (A) a diorganopolysiloxane which has a viscosity of about 50 to 500 mPa·s at 25° C. and has silicon-bonded alkenyl groups only at the molecular chain ends, (B) a diorganopolysiloxane which has a viscosity of about 50,000 to 500,000 mPa·s at 25° C. and has silicon-bonded alkenyl groups only at the molecular chain ends, (C) an organohydrogenpolysiloxane which has at least eight silicon-bonded hydrogen atoms per molecule and has a viscosity of about 3 to 15 mPa·s at 25° C., and (D) a catalytic amount of a platinum-group metal catalyst as essential components, wherein said composition has a viscosity of about 100 to 1,000 mPa·s at 25° C.; and a sheet having a releasability comprising a cured coating film of the composition.
1. A curable silicone composition which comprises:
(A) 100 parts by weight of a diorganopolysiloxane represented by the following formula (1):
wherein R 1 's each represent an alkenyl group; R's may be the same or different, each represent a monovalent hydrocarbon group having no aliphatic unsaturated bond; p and q each are 0 or a positive integer, and p+q satisfies 35≦p+q≦350; and a is an integer satisfying 1≦a≦6,
said diorganopolysiloxane having a viscosity of about 50 to 500 mPa·s at 25° C. and having silicon-bonded alkenyl groups only at the molecular chain ends;
(B) about 3.0 to 15.0 parts by weight of a diorganopolysiloxane represented by the following formula (2):
wherein R 1 's each represent an alkenyl group; R's may be the same or different, each represent a monovalent hydrocarbon group having no aliphatic unsaturated bond; r and s each are 0 or a positive integer, and r+s satisfies 1,000≦r+s≦3,000; and b is 0 or 1,
said diorganopolysiloxane having a viscosity of about 50,000 to 500,000 mPa·s at 25° C. and having silicon-bonded alkenyl groups only at the molecular chain ends;
(C) about 1.0 to 10.0 parts by weight of an organohydrogenpolysiloxane having at least eight silicon-bonded hydrogen atoms per molecule and having a viscosity of about 3 to 15 mPa·s at 25° C., the organohydrogenpolysiloxane (C) being represented by the following formula (3):
wherein H represents a hydrogen atom; R's may be the same or different, each represent a monovalent hydrocarbon group having no aliphatic unsaturated bond; t and u each are 0 or a positive integer, and t+u satisfies 8≦t+u≦25; c is 0 or 1 wherein c is 1 when b in the formula (2) is 0; and α is 0 or 1; and
(D) a catalytic amount of a platinum-group metal catalyst,
wherein said composition has a viscosity of about 100 to 1,000 mPa·s at 25° C.
2. The curable silicone composition according to claim 1 , which does not substantially contain an organic solvent.
3. The curable silicone composition according to claim 1 , which does not substantially contain an organic solvent.
4. A sheet having a releasability, which comprises a substrate and a cured coating film of said composition according to any one of claims 1 and 2 to 3 .