View Patent ↗The present invention is in the field of thermoplastic polymeric compositions, and, specifically, the present invention is in the field of poly(vinyl butyral) formation, storage, and use in multiple layer glazing panel interlayers, among other uses.
1. A thermoplastic polymer pellet comprising plasticized poly(vinyl butyral) and an antiblocking agent, wherein said antiblocking agent is a fatty acid amide having the general formula:
wherein R defines an anti-blocking segment comprising a hydrocarbon chain having about 12 to about 40 carbon atoms, and R' defines H or a hydrocarbon chain having 1 to about 40 carbon atoms.
2. The pellet of claim 1 , wherein said fatty acid amide is selected from the group consisting of erucamide, behenamide, oleyl palmitamide, stearyl erucamide, erucyl stearamide, hydroxystearamide, oleic acid diethanolamide, stearic acid diethanolamide, poly(ethylene glycol) oleic amide, octadecanamide, and mixtures of the foregoing.
3. The pellet of claim 1 , wherein said fatty acid amide is a mono-amide.
4. The pellet of claim 1 , wherein said fatty acid amide is a secondary mono-amide.
5. The pellet of claim 1 , wherein said fatty acid amide is 0.001 to 6.0 weight percent of said pellet.
6. The pellet of claim 1 , wherein said fatty acid amide is 0.01 to 0.6 weight percent of said pellet.
7. The pellet of claim 1 , wherein said fatty acid amide is 0.1 to 0.3 weight percent of said pellet.
8. The pellet of claim 1 , wherein said fatty acid amide is N-oleyl palmitamide.
9. The pellet of claim 8 , wherein said fatty acid amide is 0.001 to 6.0 weight percent of said pellet.
10. The pellet of claim 8 , wherein said fatty acid amide is 0.01 to 0.6 weight percent of said pellet.
11. The pellet of claim 8 , wherein said fatty acid amide is 0.1 to 0.3 weight percent of said pellet.
12. The pellet of claim 1 , wherein said pellet is from 0.1 milligrams to 5 grams.
13. The pellet of claim 1 , wherein said pellet is from 0.5 milligrams to 0.5 grams.
14. The pellet of claim 1 , wherein said antiblocking agent is up to 6% of said pellet.
15. A method of manufacturing a plasticized poly(vinyl butyral) pellet, comprising:
forming a melt comprising poly(vinyl butyral), a plasticizer, and an antiblocking agent; and,
forming said pellet from said melt, wherein said antiblocking agent is a fatty acid amide having the general formula:
wherein R defines an anti-blocking segment comprising a hydrocarbon chain having about 12 to about 40 carbon atoms, and R′ defines H or a hydrocarbon chain having 1 to about 40 carbon atoms.
16. A method of manufacturing a polymeric object, compnsing:
providing a thermoplastic polymer pellet comprising plasticized poly(vinyl butyral) and an antiblocking agent;
heating said pellet to form a melt; and,
using said melt to form said object, wherein said antiblocking agent is a fatty acid amide having the general formula:
wherein R defines an anti-blocking segment comprising a hydrocarbon chain having about 12 to about 40 carbon atoms, and R′ defines H or a hydrocarbon chain having 1 to about 40 carbon atoms.