View Patent ↗We have found a novel spray-on adhesive composition made from components including a high melt index polymer and a high melt tackifier that interact to produce a composition that can form a low odor, light color, non-tacky, hot melt adhesive material that can be used in disposable article manufacture. The adhesive is thermally stable at hot melt application conditions, is low in cost, is easily applied and produces high quality disposable articles.
1. A disposable diaper comprising a polyolefin film layer bonded to a synthetic non-woven layer using a low odor hot melt construction adhesive, the adhesive penetrating the fiber of the non-woven layer to embed the fiber in the adhesive, the construction adhesive comprising:
(a) greater than about 40 wt % of a copolymer comprising an ethylene vinyl acetate copolymer having 27±5 wt. % vinyl acetate having a melt index greater than 800 gm-10 min −1 ; and
(b) an effective amount less than 40 wt.-% of a tackifying resin with a softening point greater than about 100° C.; and
(c) 0 wt % to 5 wt % of a wax,
wherein the weight ratio of the copolymer to the tackifying resin is greater than about 1:1 and the construction adhesive provides an initial adhesion between the polyolefin film layer and the synthetic nonwoven layer of at least 90 g when applied by spiral spray to the polyolefin film layer at about 1 to 8 milligrams of adhesive per square inch.
2. The disposable diaper of claim 1 wherein the adhesive has a softening point of less than about 95° C.
3. The disposable diaper of claim 1 wherein the weight ratio is greater than 1.5:1 and the adhesive has a softening point less than 85° C.
4. The disposable diaper of claim 1 wherein the weight ratio is greater than 1.8:1.
5. The disposable diaper of claim 1 wherein the copolymer comprises a blend of a first copolymer having about 15 to 22 wt % vinyl acetate monomer present in the first copolymer and a second copolymer having about 23 to 30 wt % vinyl acetate, present in the second copolymer.
6. The disposable diaper of claim 1 wherein the ethylene vinyl acetate copolymer has a vinyl acetate content of about 25 to 35 wt % vinyl acetate and the ethylene vinyl acetate copolymer is present in the adhesive at a weight ratio polymer to resin of at least 2:1.
7. The disposable diaper of claim 1 wherein the construction adhesive comprises copolymer in an amount of about 60 to 85 wt % based on the weight of the construction adhesive.
8. The disposable diaper of claim 7 wherein the copolymer has a melt index greater than 2700 gm-10 min −1 .
9. The disposable diaper of claim 7 wherein the construction adhesive comprises tackifying resin in an amount of 20 to 40 wt % based on the weight of the construction adhesive.
10. The disposable diaper of claim 1 wherein the adhesive has a viscosity of 4000 to 8000 cP at 150° C.
11. The disposable diaper of claim 1 wherein the tackifying resin comprises a blend of a first tackifier and a second tackifier wherein the first tackifier has a melting point 5° C. different than the second tackifier.
12. The disposable diaper of claim 1 wherein the tackifying resin comprises an hydrogenated hydrocarbon tackifying resin.
13. A disposable diaper comprising a film layer bonded to a non-woven layer using a hot melt construction adhesive, the adhesive penetrating the fiber of the non-woven layer to embed the fiber in the adhesive, the construction adhesive comprising:
(a) about 55 wt % to 65 wt % of a copolymer comprising an ethylene vinyl acetate copolymer wherein the copolymer has about 27±5 wt % vinyl acetate content and a melt index of about 800 gm-10 min −1 to 1000 gm-10 min −1 ; and
(b) about 35 wt % to 45 wt % of a tackifying resin with a softening point of about 85° C. to 110° C.; and
(c) 0 wt % to 5 wt % of a wax; wherein the weight ratio of the copolymer to the tackifying resin is greater than about 1:1 and the construction adhesive provides an initial adhesion between the polyolefin film layer and the synthetic nonwoven layer of at least 90 g when applied by spiral spray to the polyolefin film layer at about 1 to 8 milligrams of adhesive per square inch.
14. The disposable diaper of claim 13 wherein the softening point of the construction adhesive is about 70° C. to 85° C.
15. The disposable diaper of claim 13 wherein the tackifier is an aromatically modified cycloaliphatic hydrocarbon.
16. A disposable diaper comprising a film layer bonded to a non-woven layer using a hot melt construction adhesive, the adhesive penetrating the fiber of the non-woven layer to embed the fiber in the adhesive, the construction adhesive comprising:
(a) about 65 wt % to 75 wt % of a copolymer comprising an ethylene α-olefin copolymer, an ethylene vinyl acetate copolymer with 27±5 wt % vinyl acetate, an ethylene methyl methacrylate copolymer, or mixtures thereof having a melt index of about 2000 gm-10 min −1 to 2500 gm-10 min −1 ; and
(b) about 25 wt % to 35 wt % of a low odor tackifying resin with a softening point of about 85° C. to 110° C.; and
(c) 0 wt % to 5 wt % of a wax; wherein the weight ratio of the copolymer to the tackifying resin is greater than about 1:1 and the construction adhesive provides an initial adhesion between the polyolefin film layer and the synthetic nonwoven layer of at least 90 g when applied by spiral spray to the polyolefin film layer at about 1 to 8 milligrams of adhesive per square inch.
17. The disposable diaper of claim 16 wherein the softening point of the construction adhesive is about 70° C. to 85° C.
18. The disposable diaper of claim 16 wherein the tackifier is an aromatically modified cycloaliphatic hydrocarbon.