Variable case depth powder metal gear and method thereof
View Patent ↗A gear and a method of making a forged powder metal gear having a plurality of teeth and a variable case depth profile forged in the plurality of teeth. Each tooth of the plurality of teeth has a first surface and a tooth root. A variable case depth profile is formed in each tooth of the plurality of teeth, whereby the variable case depth profile exhibits greater tooth wear resistance on the first surface and greater impact resistance in the tooth root.
1. A method for obtaining a bevel gear made from powder metal having a variable case depth profile formed in a plurality of teeth comprising the sequential steps of:
compacting a metal powder into a preform having a nearly uniform initial carbon content throughout said preform, said preform having at least one cross-sectional surface desired to have a variable case depth profile;
sintering and carburizing, sequentially or simultaneously, said preform at a desired temperature, said carburizing substantially increasing an initial carbon content to provide a controlled carbon atmosphere, and maintaining said preform in said controlled atmosphere for a predetermined period of time to obtain an initial carbon case having a substantially constant carbon case depth;
forging said preform in a forge at a forge temperature and a forge pressure to obtain a substantially dense and near net shape forged part with said variable case depth profile symmetrical about said plurality of teeth, wherein said variable case depth profile is achieved by utilizing a die set of the forge to variably enhance critical flow of metal, said die set being shaped to cause some portions of said initial carbon case in said plurality of teeth to be stretched and thinned and other portions of said initial carbon case in said plurality of teeth to be thickened and deepened during forging of said plurality of teeth; and
cooling said forged part;
wherein said plurality of teeth of said bevel gear extend radially in the same general direction as a rotational axis of said bevel gear, but are inclined with respect to said rotational axis, such that during forging the die set forges said plurality of teeth at an angle relative to said rotational axis.
2. The method of claim 1 further comprising preheating said preform to a pre-forge temperature prior to forging, and cooling said forged part by quenching.
3. The method of claim 1 further comprising dwelling said forged part for a dwell period to allow for temperature stabilization after forging and prior to quenching.
4. The method of claim 1 further comprising splining said gear after cooling.
5. The method of claim 1 comprising, after cooling, performing at least one of scaling, surfacing, turning, and shot peening on said forged part.
6. The method of claim 1 wherein said metal powder is a low alloy ferrous metal powder.
7. The method of claim 1 wherein said gear is near net shape after forging and cooling.
8. The method of claim 1 , wherein said variable case depth profile for at least one tooth in the plurality of teeth has a case depth at a tip of the tooth that is greater than a case depth at a corresponding root of the tooth and further has a case depth at a root fillet surface, between the tip and the corresponding root of the tooth, that is less than both the case depth of the tip and the case depth of the corresponding root.