Mid-range vinylidene content polyisobutylene polymer product produced by liquid phase polymerization process
View Patent ↗A mid-range vinylidene content PIB polymer composition made by a liquid phase polymerization process conducted in a loop reactor at a temperature of at least 60° F. using a BF 3 /methanol catalyst complex and a contact time of no more than 4 minutes. At least about 90% of the PIB molecules present in the product comprise alpha or beta position isomers. The vinylidene (alpha) isomer content of the product may range from 20% to 70% thereof, and the content of tetra-substituted internal double bonds is very low, advantageously no more than about 10%, preferably less than about 5% and ideally less than about 1-2%.
1. A mid-range vinylidene content PIB polymer composition comprising PIB molecules, wherein a first portion of said PIB molecules have alpha position double bonds and a second portion of said PIB molecules have beta position double bonds, wherein said first and second portions together include at least 90% of the PIB molecules of the composition, wherein no more than about 10% of the PIB molecules of the composition have tetra-substituted internal double bonds, wherein said first portion comprises less than 70% of the PIB molecules of the composition, and wherein said composition has a polydispersity of no more than 2.0, said PIB polymer composition characterized by having been prepared by a process comprising:
providing a liquid feedstock comprising isobutylene;
providing a catalyst composition comprising a stable complex of BF 3 and a catalyst complexing agent, wherein the ratio of complexing agent to BF 3 in said complex is no more than about 1.3:1;
introducing said feedstock and said catalyst composition into a residual reaction mixture in a loop reactor reaction zone;
recirculating the residual reaction mixture in said zone at a recirculation rate sufficient to cause intimate intermixing of the residual reaction mixture, the feedstock and the catalyst composition to thereby present a recirculating, intimately intermixed reaction admixture in said reaction zone;
maintaining the recirculating intimately intermixed reaction admixture in its intimately intermixed condition and removing heat of reaction from the reaction admixture at a rate calculated to provide a substantially constant reaction temperature in the reaction admixture while the same is recirculating in said reaction zone;
withdrawing a product stream comprising said mid-range vinylidene content PIB polymer composition; and
controlling the introduction of said feedstock into said reaction zone and the withdrawal of said product stream from the reaction zone such that the residence time of the isobutylene components undergoing polymerization in the reaction zone is no more than about 4 minutes.
2. A mid-range vinylidene content PIB polymer composition as set forth in claim 1 , wherein said reaction temperature is at least about 60 ° F., and wherein said agent is methanol.
3. A mid-range vinylidene content PIB polymer composition as set forth in claim 1 , wherein the ratio of complexing agent to BF3 in said complex is about 1:1.
4. A mid-range vinylidene content PIB polymer composition having an alpha position double bond content that is less than 70% of the total double bond content of the composition and a polydispersity of no more than 2.0, said composition characterized by having been produced by a process comprising:
providing a feedstock comprising isobutylene;
providing a catalyst composition comprising a complex of BF 3 and a complexing agent therefor;
introducing said feedstock and said catalyst composition into a residual reaction mixture in a reaction zone;
intimately intermixing said residual reaction mixture, said feedstock and said catalyst composition to present an intimately intermixed reaction admixture in said reaction zone;
maintaining the intimately intermixed reaction admixture in its intimately intermixed condition and keeping it at a temperature of at least about 0 ° C. while the same is in said reaction zone, to thereby cause the isobutylene therein to undergo polymerization to form said polyisobutylene;
manipulating the ratio of BF 3 to complexing agent in the catalyst composition so as to adjust the vinylidene content of the PIB polymer composition;
withdrawing a product stream comprising polyisobutylene having an alpha plus beta isomer content of at least about 90% from said reaction zone; and
controlling the introduction of said feedstock into said reaction zone and the withdrawal of said product stream from the reaction zone such that the residence time of the isobutylene undergoing polymerization in the reaction zone is no greater than about 4 minutes.