Composition for vulcanized rubber and vulcanization product
A composition for epihalohydrin vulcanized rubber excellent in heat resistance while keeping good vulcanization rate and store stability, comprising (a) an epihalohydrin robber, (b) a metal soap, (c) an acid acceptor, and (d) a vulcanizing agent, the composition further preferably containing (e) a fatty acid for suppressing vulcanization, or preferably containing (f) an alcohol for accelerating vulcanization.
1. A composition for vulcanized rubber comprising (a) 100 parts by weight of an epihalohydrin rubber, (b) 0.3 to 5 parts by weight of sodium salt and/or potassium salt of a fatty acid having 12 to 24 carbon atoms, (c) 1 to 20 parts by weight of an acid acceptor, wherein the acid acceptor is synthetic hydrotalcites, and (d) 0.3 to 5 parts by weight of a vulcanizing agent, wherein the vulcanizing agent is a quinoxaline vulcanizing agent.
2. A composition for vulcanized rubber according to claim 1 , further containing (e) 0.1 to 3 parts by weight of a fatty acid and/or (f) 0.1 to 3 parts by weight of an alcohol.
3. A composition for vulcanized rubber according to claim 1 , wherein the sodium salt and/or potassium salt of fatty acid having 12 to 24 carbon atoms is sodium stearate salt and/or potassium stearate.
4. A composition for vulcanized rubber according to claim 1 , wherein the vulcanizing agent is 6-methyl quinoxaline-2,3-dithiocarbonate.
5. A vulcanized product obtained by vulcanizing the composition for vulcanized rubber according to claim 1 .
6. A rubber part for use in automobiles comprising the vulcanized product according to claim 5 .