Brazing method of an aluminum material
A method of brazing an aluminum material, which contains: using an aluminum alloy brazing sheet, wherein an aluminum alloy containing 0.2 to 1 mass % of Mg is used for a core alloy; the brazing sheet, in which an Mg amount in a filler alloy is 0.05 mass % or less, is used; and the brazing is carried out by using a brazing furnace that has at least two chambers for brazing in an inert gas atmosphere under a heating condition of a temperature-rising time of within 12 minutes from a temperature exceeding 200° C., to 570° C.; a brazing furnace and an aluminum alloy brazing sheet, each of which is used in the method; and a heat exchanger, which is produced by the method.
1 . A method of brazing an aluminum material, comprising: using an aluminum alloy brazing sheet, wherein an aluminum alloy comprising 0.2 mass % or more but 1 mass % or less of Mg is used for a core alloy; said brazing sheet, in which an Mg amount in a filler alloy is 0.05 mass % or less, is used; and said brazing is carried out by using a brazing furnace that comprises at least two chambers for brazing in an inert gas atmosphere under a heating condition of a temperature-rising time of within 12 minutes from a temperature exceeding 200° C., to 570° C.
2 . The brazing method according to claim 1 , wherein an oxygen concentration in the chamber for heating at a temperature equal to or lower than the melting point of the filler alloy is 20 ppm or less.
3 . The brazing method according to claim 1 , wherein carbon is placed in the chamber for heating at a temperature equal to or lower than the melting point of the filler alloy.
4 . The brazing method according to claim 2 , wherein carbon is placed in the chamber for heating at a temperature equal to or lower than the melting point of the filler alloy.
5 . A brazing furnace, which is used in the brazing method according to claim 3 , wherein the chamber for heating at a temperature equal to or lower than the melting point of the filler alloy is constituted using carbon.
6 . The brazing furnace according to claim 5 , wherein an oxygen concentration in the chamber for heating at a temperature equal to or lower than the melting point of the filler alloy is to be set 20 ppm or less.
7 . An aluminum alloy brazing sheet, which is used in the brazing method according to claim 1 , comprising: using an aluminum alloy comprising 0.2 mass % or more but 1 mass % or less of Mg for a core alloy; and using a filler alloy, in which an Mg amount in a filler alloy is 0.05 mass % or less.
8 . A heat exchanger, which is produced by the method according to claim 1 , by using a brazing sheet, wherein said brazing sheet is to be used in the brazing method according to claim 1 , said brazing sheet comprising: an aluminum alloy comprising 0.2 mass % or more but 1 mass % or less of Mg to be used for a core alloy; and a filler alloy, in which an Mg amount in said filler alloy is 0.05 mass % or less.