Process for removing fluorosurfactant from aqueous fluoropolymer dispersions and reducing scum formation
View Patent ↗A process for reducing fluorosurfactant content of a stabilized fluorosurfactant-containing aqueous fluoropolymer dispersion containing ferric ions by contacting the fluoropolymer dispersion with strong base anion exchange resin to reduce fluorosurfactant content to a predetermined level, the anion exchange resin being in the hydroxide form, separating the dispersion from the anion exchange resin, and adding an effective amount of chelating agent having an equilibrium constant when complexed with iron of at least 10 18 prior to the contacting with the ion exchange resin for complexing ferric ions to prevent scum formation.
1. A process for reducing fluorosurfactant content of a stabilized fluorosurfactant-containing aqueous fluoropolymer dispersion containing ferric ions comprising:
contacting said fluorosurfactant-containing aqueous fluoropolymer dispersion with strong base anion exchange resin to reduce fluorosurfactant content to a predetermined level, said anion exchange resin being in the hydroxide form,
separating said anion exchange resin from said dispersion after the fluorosurfactant content has been reduced; and
adding an effective amount of chelating agent having an equilibrium constant of at least 10 18 when said chelating agent is complexed with iron prior to said contacting with said anion exchange resin for complexing ferric ions to prevent scum formation.
2. The process of claim 1 wherein said chelating agent is ethyl enediamine tetraacetic acid or salt thereof.
3. The process of claim 2 wherein said ethylenediamine tetraacetic acid or salt is added to said dispersion in an amount of about 2 to about 100 ppm.
4. The process of claim 1 wherein said effective amount of chelating agents is sufficient to complex ferric ions in said dispersion but is not in substantial excess causing competition with fluorosurfactant for ion exchange cites of said anion exchange resin.
5. The process of claim 1 wherein said anion exchange resin comprises a polymer having functional groups comprising quaternary ammonium groups.
6. The process of claim 1 wherein said contacting said fluorosurfactant-containing aqueous fluoropolymer dispersion with anion exchange resin reduces fluorosurfactant content to no greater than 300 ppm.
7. The process of claim 1 wherein said contacting said fluorosurfactant-containing aqueous fluoropolymer dispersion with anion exchange resin reduces fluorosurfactant content to no greater than 100 ppm.
8. The process of claim 1 wherein said contacting said fluorosurfactant-containing aqueous fluoropolymer dispersion with anion exchange resin reduces fluorosurfactant content to no greater than 50 ppm.