Interlayers for laminated safety glass with superior de-airing and laminating properties and process for making the same
View Patent ↗This invention relates to thermoplastic interlayers for laminated safety glass with superior vacuum de-airing at elevated temperatures and superior tacking and edge sealing properties. The sheeting has surface pattern on at least one of the surfaces characterized by flat surfaces with substantially uninterrupted channels for airflow in at least two non-parallel directions. The channels allow for rapid de-airing while the area roughness parameter ratio AR p /AR t in the range of 0.52 to 0.62, ARt being less than 32 μm, and area kurtosis less than 2.5, allow for ease of tacking of the interlayer onto glass and edge sealing after de-airing has been completed. Said surface pattern may also be superimposed onto a pattern which is generated by melt fracture or other means on at least one side to enhance de-airing and aid edge sealing.
1. A thermoplastic interlayer having an embossed surface pattern wherein the pattern provides relatively uninterrupted channels for de-airing in at least two non-parallel directions, said channels having depth of less than about 20 μm, and width about 30 μm to about 300 μm and spaced between about 0.1 mm and about 1 mm apart, and said surface pattern has roughness parameters such that the area roughness peak height (ARp) is less than 32 μm, and the ratio of the area peak height (ARp) to area roughness (ARt) is between 0.52 and 0.62, and the area kurtosis (AKu) is less than 5, wherein said interlayer is an ionoplastic polymer.
2. The thermoplastic interlayer of claim 1 wherein the width is about 40 to about 250 μm.
3. The thermoplastic interlayer of claim 1 wherein the width is about 50 to about 200 μm.
4. The thermoplastic interlayer of claim 1 wherein the surface channels are spaced between about 0.1 to about 0.9 mm apart.
5. The thermoplastic interlayer of claim 1 wherein the surface channels are spaced about 0.15 to about 0.85 mm apart.
6. The thermoplastic interlayer of claim 1 wherein the ionoplastic polymer is an ionomeric derivative of an ethylene/acid copolymer made with methacrylic acid.
7. A thermoplastic interlayer having an embossed surface pattern wherein the pattern provides relatively uninterrupted channels for de-airing in at least two non-parallel directions, said channels having depth of from about 12 to about 20 μm, and width about 30 μm to about 300 μm and spaced between about 0.1 mm and about 1 mm apart, and said surface pattern has roughness parameters such that the area roughness peak height (ARp) is less than 32 μm, and the ratio of the area peak height (AR p ) to total area roughness (ARt) is between 0.52 and 0.62, and the area kurtosis (AKu) is less than 5, wherein said interlayer is an ionoplastic polymer.
8. The thermoplastic interlayer of claim 7 wherein the interlayer has a surface pattern having a depth of from 14 to 20 μm.
9. The thermoplastic interlayer of claim 7 wherein the width is about 40 to about 250 μm.
10. The thermoplastic interlayer of claim 9 wherein the surface channels are spaced between about 0.1 to about 0.9 mm apart.
11. The thermoplastic interlayer of claim 10 wherein the ionoplastic polymer is an ionomeric derivative of an ethylene/acid copolymer made with methacrylic acid.
12. The thermoplastic interlayer of claim 7 wherein the width is about 50 to about 200 μm.
13. The thermoplastic interlayer of claim 12 wherein the surface channels are spaced about 0.15 to about 0.85 mm apart.
14. The thermoplastic interlayer of claim 7 wherein the surface channels are spaced between about 0.1 to about 0.9 mm apart.
15. The thermoplastic interlayer of claim 7 wherein the surface channels are spaced about 0.15 to about 0.85 mm apart.
16. A sheet of unplasticized thermoplastic ionoplastic polymer interlayer, which prior to lamination comprises at least one surface comprising an embossed surface pattern which provides relatively uninterrupted channels for de-airing in at least two non-parallel directions, said channels having depth of up to about 20 μm, and width 30 μm to 300 μm and spaced between 0.1 mm and 1 mm apart.
17. The thermoplastic interlayer of claim 16 wherein said interlayer has a surface pattern having a depth of from 12 to 20 μm.
18. The thermoplastic interlayer of claim 17 wherein the surface pattern has roughness parameters such that the area roughness peak height (ARp) is less than 32 μm, and the ratio of the of area peak height (AR p ) to total area roughness (ARt) is between 0.42 and 0.62, and the area kurtosis (AKu) is less than 5.
19. The thermoplastic interlayer of claim 17 which is embossed on one side of the interlayer.
20. The thermoplastic interlayer of claim 17 which is embossed on both sides of the interlayer.
21. The thermoplastic interlayer of claim 20 wherein the embossed pattern on one side of the interlayer sheet has a depth of 12 to 20 μm and the pattern is orthogonal to the edges of the sheet, while the embossed pattern on the other side of the interlayer sheet is an identical embossed pattern but is slanted at some angle that is greater than or less than 9° to the edges.
22. The thermoplastic interlayer of claim 20 wherein the embossing pattern and/or the depth thereof of the two sides are asymmetric with respect to each other.
23. The thermoplastic interlayer of claim 17 said channels having depth of from 12 to less than 20 μm.
24. The thermoplastic interlayer of claim 16 wherein said Interlayer has a surface pattern having a depth of from about 14 to about 20 μm.
25. The thermoplastic interlayer of claim 16 wherein the ionoplastic polymer is an ionomeric derivative of an ethylene/acid copolymer made with methacrylic acid.