A method for controlling the foaming of slag in an electric arc furnace is disclosed. The furnace comprises at least one electrode column. Current is applied to the electrode column, causing an arc to form between the tip of the electrode column and the scrap, melting the scrap. Impurities in the molten scrap metal rise to the surface forming slag. A meter determines the total harmonic distortion associated with the system. If the total harmonic distortion is greater than a predetermined set point, and the scrap metal is sufficiently molten, then a foaming agent is added thereto.
1 . A method for making steel in an electric arc furnace, the electric arc furnace containing scrap metal to be melted, the scrap metal having impurities therein, the method comprising the following steps:
providing at least one electrode column moveable into and out of the electric arc furnace;
applying current to the electrode column so as to cause an arc to form between the electrode column and the scrap metal, which arc causes the scrap metal to melt, wherein the impurities in the molten scrap metal rise to the surface thereof to form a slag, the applied current causing at least some harmonic distortion;
determining a total harmonic distortion value from the at least some harmonic distortion;
determining if the total harmonic distortion value is greater than a predetermined set point; and
adding at least one foaming agent to the slag if the total harmonic distortion value is greater than the predetermined set point.
2 . The method of claim 1 , further comprising the step of automatically adding foaming agent to the slag if the total harmonic distortion value is greater than the predetermined set point.
3 . The method of claim 2 , determining the amount of current that has been applied to the at least one electrode and from that determining a total amount electrical energy that has been applied to the furnace, then determining if the total amount of electrical energy is greater than a predetermined amount.
4 . The method of claim 3 , adding foaming agent to the slag if the total amount electrical energy that has been applied is greater than the predetermined amount.
5 . The method of claim 2 , further comprising the step of providing a lance through which the foaming agent may be added to the slag.
6 . The method of claim 5 , further comprising the step of determining if the lance is a predetermined proper position.
7 . The method of claim 6 , further comprising the step of adding foaming agent to the slag if the lance is in the predetermined proper position.
8 . The method of claim 1 , further comprising the step of manually adding foaming agent to the slag if the total harmonic distortion value is greater than the predetermined set point.
9 . The method of claim 8 , wherein the foaming agent comprises carbon, coke, graphite powder, lime, MgO or a combination thereof.
10 . A method for foaming slag in an electric arc furnace containing scrap metal, the method comprising the following steps:
providing at least one electrode column moveable into and out of the electric arc furnace;
applying current to the electrode column so as to cause an arc to form between the electrode column and the scrap metal, which current is high enough to cause the scrap metal to melt, wherein the impurities in the molten scrap metal rise to the surface thereof to form a slag, wherein the applied current causes at least some harmonic distortion from which an amount of total harmonic distortion may be determined, wherein an amount of total electrical energy may be determined from the current applied;
determining the total harmonic distortion;
determining if the total harmonic distortion is greater than a predetermined set point;
determining the total electrical energy;
determining if the total electrical energy is greater than a predetermined set point;
providing a lance movable into and out of an appropriate position;
determining if the lance is in an appropriate position; and
adding a foaming agent through the lance to the slag if the total harmonic distortion is greater than the predetermined set point, the total electrical energy is greater than a predetermined set point, and the lance is in the appropriate position.
11 . The method of claim 10 , further comprising the step of automatically adding foaming agent to the slag.
12 . The method of claim 10 , further comprising the step of adding foaming agent to the slag for a predetermined amount of time.
13 . The method of claim 12 , further comprising the step of adding the foaming agent to the slag for about ten seconds.
14 . The method of claim 10 , further comprising the step of periodically and automatically monitoring the total harmonic distortion.
15 . The method of claim 14 , further comprising the step of continuously and automatically monitoring the total harmonic distortion.
16 . The method of claim 10 , wherein the foaming agent comprises carbon, coke, graphite powder, lime, MgO or a combination thereof.
17 . The method of claim 10 , further comprising the step of manually adding foaming agent to the slag.