Partial-discharge-resistant insulating varnish, insulated wire and method of making the same

1. A partial-discharge-resistant insulating varnish, comprising:

a polyamide-imide enamel varnish comprising a polyamide-imide resin and a solvent component used for a synthesis reaction of the polyamide-imide enamel varnish, the solvent component comprising 67% to 87% by weight of γ-butyrolactone and a balance consisting of 1) at least one of N-methyl-2-pyrrolidone and N,N-dimethylformamide, or 2) cyclohexanone and N,N-dimethylformamide; and

an organo-silica sol comprising silica and a dispersion solvent component comprising at least one selected from the group consisting of γ-butyrolactone, benzyl alcohol and solvent naphtha,

wherein a total amount of γ-butyrolactone comprised in the solvent component and the dispersion solvent component is 50% or more and less than 100% by weight relative to a total amount of the solvent component and the dispersion solvent component.

2. The partial-discharge-resistant insulating varnish according to claim 1 , wherein:

a silica component of the organo-silica sol is 1 to 100 phr (parts per hundred parts of resin) by weight to a resin component of the polyamide-imide enamel varnish.

3. The partial-discharge-resistant insulating varnish according to claim 1 , wherein:

the organo-silica sol has an average particle size of 100 nm or less.

4. The partial-discharge-resistant insulating varnish according to claim 1 , wherein:

the organo-silica sol has an average particle size of 30 nm or less.

5. The partial-discharge-resistant insulating varnish according to claim 1 , wherein:

the organo-silica sol is uniformly dispersed in the polyamide-imide enamel varnish.

6. The partial-discharge-resistant insulating varnish of claim 1 , wherein the total amount of the solvent component and the dispersion solvent component comprises cyclohexanone and 50% or more by weight of γ-butyrolactone.

7. The partial-discharge-resistant insulating varnish of claim 1 , wherein the total amount of the solvent component and the dispersion solvent component comprises NMP and 50% or more by weight of γ-butyrolactone.

8. The partial-discharge-resistant insulating varnish of claim 1 , wherein the total amount of the solvent component and the dispersion solvent component comprises benzyl alcohol, solvent naphtha and 50% or more by weight of γ-butyrolactone.

9. The partial-discharge-resistant insulating varnish of claim 1 , wherein the total amount of the solvent component and the dispersion solvent component comprises cyclohexanone, benzyl alcohol, solvent naphtha and 50% or more by weight of γ-butyrolactone.

10. The partial-discharge-resistant insulating varnish of claim 1 , wherein the total amount of the solvent component and the dispersion solvent component comprises 50% or more by weight of γ-butyrolactone and at least one selected from the group consisting of: polar solvent, aromatic hydrocarbon, and lower alcohol.

11. The partial-discharge-resistant insulating varnish of claim 1 , wherein the total amount of the solvent component and the dispersion solvent component comprises 50% or more by weight of γ-butyrolactone; and at least one selected from the group consisting of: NMP, DMF, cyclohexanone, benzyl alcohol, and solvent naphtha.

12. The partial-discharge-resistant insulating varnish of claim 1 , wherein the total amount of the solvent component and the dispersion solvent component comprises 50% or more by weight of γ-butyrolactone and at least two selected from the group consisting of: NMP, DMF, cyclohexanone, benzyl alcohol, and solvent naphtha.

13. The partial-discharge-resistant insulating varnish of claim 1 , wherein the γ-butyrolactone is a main solvent of the polyamide-imide enamel varnish and is a main dispersion solvent of the organo-silica sol.

14. The partial-discharge-resistant insulating varnish of claim 1 , wherein an amount of moisture in the organo-silica sol is 1.0% or less.

15. The partial-discharge-resistant insulating varnish of claim 1 , wherein the organo-silica sol has a silica concentration of 20% or more.

16. The partial-discharge-resistant insulating varnish of claim 1 , wherein the organo-silica sol is dispersed in the polyamide-imide enamel varnish under a dispersing condition that when a 10 kHz of frequency and 1 kV of voltage are applied to an enameled wire that has not been substantially elongated, 76.8 h or more of a V-t characteristic can be obtained.

17. The partial-discharge-resistant insulating varnish of claim 1 , wherein the organo-silica sol is dispersed in the polyamide-imide enamel varnish under a dispersing condition that when a 10 kHz of frequency and 1 kV of voltage are applied to an enameled wire that has been elongated 20%, 42.8 h or more of a V-t characteristic can be obtained.

18. The partial-discharge-resistant insulating varnish according to claim 1 , wherein an amount of γ-butyrolactone comprised in the dispersion solvent component is less than an amount of γ-butyrolactone comprised in the solvent component.

19. The partial-discharge-resistant insulating varnish according to claim 1 , wherein the total amount of γ-butyrolactone comprised in the solvent component and the dispersion solvent component is 51.3% to 89.7% by weight relative to the total amount of the solvent component and the dispersion solvent component.

20. An insulated wire, comprising:

a conductor; and

a partial-discharge-resistant insulation coating film formed on a surface of the conductor,

wherein the partial-discharge-resistant insulation coating film is made of the partial-discharge-resistant insulating varnish of claim 1 , and

wherein the partial-discharge-resistant insulation coating film has 76.8 h or more of a V-t characteristic when a 10 kHz of frequency and 1.0 kV of voltage are applied to the insulated wire that has not been substantially elongated, and the partial-discharge-resistant insulation coating film has 42.8 h or more of the V-t characteristic when a 10 kHz of frequency and 1.0 kV of voltage are applied to the insulated wire that has been elongated 20%.

21. The insulated wire according to claim 20 , wherein the silica dispersed in the polyimide-imide resin has an average particle diameter in BET method of not more than 30 nm.

22. The insulated wire according to claim 20 , wherein the silica dispersed in the polyamide-imide resin is contained in the range of 3 to 70 phr (parts per hundred parts of resin) to the polyamide-imide resin.

23. An insulated wire, comprising:

a conductor; and

a partial-discharge-resistant insulation coating film formed on a surface of the conductor,

wherein the partial-discharge-resistant insulation coating film is made of the partial-discharge-resistant insulating varnish of claim 1 , and

wherein the organo-silica sol is dispersed in the polyamide-imide enamel varnish under a dispersing condition that when a 10 kHz of frequency and 1 kV of voltage are applied to an enameled wire that has not been substantially elongated, 76.8 h or more of a V-t characteristic can be obtained.

24. An insulated wire, comprising:

a conductor; and

a partial-discharge-resistant insulation coating film formed on a surface of the conductor,

wherein the partial-discharge-resistant insulation coating film is made of the partial-discharge-resistant insulating varnish of claim 1 , and

wherein the organo-silica sol is dispersed in the polyamide-imide enamel varnish under a dispersing condition that when a 10 kHz of frequency and 1 kV of voltage are applied to an enameled wire that has been elongated 20%, 42.8 h or more of a V-t characteristic can be obtained.

25. An insulated wire, comprising:

a conductor; and

a partial-discharge-resistant insulation coating film formed on a surface of the conductor,

wherein the partial-discharge-resistant insulation coating film is made of the partial-discharge-resistant insulating varnish of claim 1 ,

wherein the partial-discharge-resistant insulation coating film comprises a polyamide-imide resin and silica dispersed in the polyamide-imide resin, and

wherein the partial-discharge-resistant insulation coating film has 76.8 h or more of a V-t characteristic when a 10 kHz of frequency and 1.0 kV of voltage are applied to the insulated wire that has not been substantially elongated, and the partial-discharge-resistant insulation coating film has 42.8 h or more of the V-t characteristic when a 10 kHz of frequency and 1.0 kV of voltage are applied to the insulated wire that has been elongated 20%.

26. A partial-discharge-resistant insulating varnish, comprising:

a polyamide-imide enamel varnish comprising a polyamide-imide resin and a solvent component used for a synthesis reaction of the polyamide-imide enamel varnish, the solvent component consisting of 67% to 87% by weight of γ-butyrolactone, and a balance consisting of N-methyl-2-pyrrolidone; and

an organo-silica sol comprising silica and a dispersion solvent component comprising at least one selected from the group consisting of γ-butyrolactone, benzyl alcohol and solvent naphtha,

wherein the total amount of γ-butyrolactone comprised in the solvent component and the dispersion solvent component is 50% or more and less than 100% by weight relative to the total amount of the solvent component and the dispersion solvent component.

27. A partial-discharge-resistant insulating varnish, comprising:

a polyamide-imide enamel varnish comprising a polyamide-imide resin and a solvent component used for a synthesis reaction of the polyamide-imide enamel varnish, the solvent component consisting of 67% to 87% by weight of γ-butyrolactone, and a balance consisting of cyclohexanone; and

an organo-silica sol comprising silica and a dispersion solvent component comprising at least one selected from the group consisting of γ-butyrolactone, benzyl alcohol and solvent naphtha,

wherein the total amount of γ-butyrolactone comprised in the solvent component and the dispersion solvent component is 50% or more and less than 100% by weight relative to the total amount of the solvent component and the dispersion solvent component.

28. A partial-discharge-resistant insulating varnish, comprising:

a polyamide-imide enamel varnish comprising a polyamide-imide resin and a solvent component used for a synthesis reaction of the polyamide-imide enamel varnish, the solvent component consisting of 67% to 87% by weight of γ-butyrolactone, and a balance consisting of cyclohexanone and N,N-dimethylformamide; and

an organo-silica sol comprising silica and a dispersion solvent component comprising at least one selected from the group consisting of γ-butyrolactone, benzyl alcohol and solvent naphtha,

wherein the total amount of γ-butyrolactone comprised in the solvent component and the dispersion solvent component is 50% or more and less than 100% by weight relative to the total amount of the solvent component and the dispersion solvent component.