Imparting high-temperature degradation resistance to components for internal combustion engine systems
View Patent ↗A method of imparting high-temperature, degradation resistance to a component associated with an internal combustion engine involving applying a metal slurry comprising a Co-based metallic composition, a binder, and a solvent to a surface of the component, and sintering the Co-based metallic composition to form a substantially continuous Co-based alloy coating on the surface of the body. An internal combustion engine component comprising a metallic substrate and a Co-based metallic coating thereon which has a thickness between about 100 and about 1000 microns.
1. A method of imparting high-temperature, degradation resistance to a combustion engine component associated with an internal combustion engine comprising:
applying a metal slurry comprising a Co-based alloy composition, a binder, and a solvent to a surface of the internal combustion engine component having a body of a material selected from the group consisting of carbon steel, stainless steel, and alloy steel, wherein the metal slurry comprises Co-based powdered alloy particles comprising between about 0.05 and about 0.5 wt % B, between about 5 and about 20 wt % Cr, between about 22 and 32 wt % Mo, between 1 and about 4 wt % Si, and balance Co, and wherein the internal combustion engine component has a sharp projection, cavity, and/or through hole; and
sintering the Co-based metallic composition to form a substantially continuous Co-based alloy coating between about 100 and about 1000 microns thick on the surface of the combustion engine component, wherein the Co-based alloy coating has a microstructure characterized by generally non-dendritic, irregularly spherical, nodular intermetallic Laves phase nodules, and wherein the coating imparts resistance to wear against mating components;
wherein said sintering is performed at a temperature in the range of 2200° F. to 2300° F.
2. The method of claim 1 wherein the Co-based alloy comprises about B-0.15%, Cr-8.5%, Mo-28%, Si-2.6%, and balance Co.
3. The method of claim 1 wherein the Co-based alloy comprises about B-0.15%, Cr-14%, Mo-26%, Si-2.6%, and balance Co.
4. The method of claim 3 wherein the coating thickness is between about 100 and about 300 microns.
5. The method of claim 3 wherein the coating thickness is between about 250 and about 300 microns.
6. The method of claim 1 wherein the Laves phase nodules comprise dispersed particles and interconnected particles, wherein interconnections between particles include a plurality of thin filamentous Laves phase interconnections between dispersed Laves phase particles.
7. The method of claim 1 wherein said sintering is performed at a temperature of 2200° F.
8. The method of claim 1 wherein said sintering is performed at a temperature of about 2300° F.
9. A method of imparting high-temperature, degradation resistance to a combustion engine component associated with an internal combustion engine comprising:
applying a metal slurry comprising solvent, binder, and metal particles of an alloy consisting essentially of between about 0.05 and about 0.5 wt % B, between about 5 and about 20 wt % Cr, between about 22 and 32 wt % Mo, between 1 and about 4 wt % Si, and balance Co to a surface of the internal combustion engine component, wherein the internal combustion engine component has a sharp projection, cavity, and/or through hole, and wherein the internal combustion engine component has a body of a material selected from the group consisting of carbon steel, stainless steel, and alloy steel; and
heating to remove the solvent and binder and to sinter the Co-based metallic composition to form a substantially continuous Co-based alloy coating on the surface of the combustion engine component, wherein the Co-based alloy coating has a microstructure characterized by a generally non-dendritic, irregularly spherical, nodular intermetallic phase, and wherein the coating imparts resistance to wear against mating components;
wherein said sintering is performed at a temperature in the range of 2200° F. to 2300° F.
10. The method of claim 9 wherein the Co-based alloy comprises about B-0.15%, Cr-17%, Mo-28%, Si-3.25%, and balance Co.
11. The method of claim 9 wherein the metal slurry consists essentially of the Co-based powdered alloy particles, the binder, and the solvent, and wherein the Co-based powdered alloy particles are an alloy consisting essentially of about B-0.15%, Cr-8.5%, Mo-28%, Si-2.6%, and balance Co.
12. The method of claim 9 wherein the Co-based alloy comprises about B-0.15%, Cr-14%, Mo-26%, Si-2.6%, and balance Co.
13. The method of claim 12 wherein the coating thickness is between about 100 and about 300 microns.
14. The method of claim 12 wherein the coating thickness is between about 250 and about 300 microns.
15. The method of claim 9 wherein said sintering is performed at a temperature of 2200° F.
16. The method of claim 9 wherein said sintering is performed at a temperature of about 2300° F.