Intumescent substrate coating
View Patent ↗An intumescent coating in the form of an initially liquid coating which cures to a solid and adheres to a substrate. The coating includes a flexible thermosetting epoxy, such as diglycidyl ether of bisphenol-A (DGEBA), with an aliphatic amine curing agent, expandable graphite flakes with reagent chemicals that react upon heating and decompose into gaseous products, and fumed silica. In the presence of heat or flame, an intumescent layer develops at the coating surface, insulating the substrate. The coating is found to add intumescent characteristics which provide heat resistant and fire retardant qualities.
1. A liquid coating formulation comprising:
(a) approximately 50% to 55% by weight of a flexible thermosetting epoxy with an aliphatic amine curing agent,
(b) approximately 40% to 45% by weight of expandable crystalline graphite flakes treated with reagent chemicals that react upon heating and decompose into gaseous products, and
(c) approximately 5% to 10% by weight fumed silica; wherein said weight percentages are based on the weight of the liquid coating formulation;
wherein the liquid coating formulation cures to an intumescent, impact resistant solid and adheres to a substrate.
2. The liquid coating formulation as set forth in claim 1 wherein said thermosetting epoxy is diglycidyl ether of bisphenol-A (DGEBA).
3. The liquid coating formulation as set forth in claim 1 wherein said fumed silica is an amorphous colloidal silicon dioxide.
4. The liquid coating formulation as set forth in claim 1 comprising:
(a) approximately 54.4% by weight of said flexible thermosetting epoxy with said aliphatic amine curing agent,
(b) approximately 40.3% by weight of said expandable crystalline graphite flakes treated with reagent chemicals that react upon heating and decompose into gaseous products, and
(c) approximately 5.3% by weight of said fumed silica.
5. A carbon reinforced epoxy composite substrate coated with and adhered to an intumescent, impact resistant solid coating; wherein the intumescent, impact resistance solid coating is a cured product of the liquid coating formulation as set forth in claim 1 .
6. A metal substrate coated with and adhered to an intumescent, impact resistant solid coating; wherein the intumescent, impact resistance solid coating is a cured product of the liquid coating formulation as set forth in claim 1 .
7. A substrate coated with and adhered to an intumescent, impact resistant solid coating; wherein the intumescent, impact resistance solid coating is a cured product of the liquid coating formulation as set forth in claim 1 and wherein said coating is between 0.02 inches and 0.2 inches thick.
8. The coated substrate as set forth in claim 7 wherein said coating is between 0.05 inches and 15 inches thick.
9. A liquid coating formulation comprising:
(a) a flexible thermosetting epoxy with an aliphatic amine curing agent,
(b) fumed silica, and
(c) expandable crystalline graphite flakes treated with reagent chemicals that react upon heating and decompose into gaseous products;
wherein the volumetric mix ratio of (a), unpacked dry (b), and unpacked dry (c) is 1:2:1; and
wherein the liquid coating formulation cures to an intumescent, impact resistant solid and adheres to a substrate.
10. The liquid coating formulation as set forth in claim 9 wherein said thermosetting epoxy is diglycidyl ether of bisphenol-A (DGEBA).
11. The liquid coating formulation as set forth in claim 9 wherein said fumed silica is an amorphous colloidal silicon dioxide.