Transparent thermoplastic antimicrobial molding composition
A transparent antimicrobial thermoplastic molding composition is disclosed. The composition contains aromatic polycarbonate resin and 0.01 to 3.8 of an antimicrobial compound conforming to formula (I) Ag a M 1 b M 2 2 (PO 4 ) 3 (I) wherein M 1 is at least one ion selected from the group consisting of alkali metal ion, alkaline earth metal ion, ammonium ion and hydrogen ion, M 2 a tetravalent metal selected from the group consisting of Ti, Zr and Sn, and where a and b are positive numbers where a+mb=1 where m is a valence of M 1 , the percent being relative to the weight of the polycarbonate. The composition is suitable for molding articles having good appearance and surface qualities.
1. A transparent thermoplastic molding composition comprising aromatic polycarbonate resin and 0.01 to 3.8 weight percent of an antimicrobial compound conforming to formula (I)
Ag a M 1 b M 2 2 (PO 4 ) 3 (I)
wherein M 1 is at least one ion selected from the group consisting of alkali metal ion, alkaline earth metal ion and ammonium ion, M 2 is a tetravalent metal selected from the group consisting of Ti, Zr and Sn, a and b are positive numbers and a+mb=1 where m is a valence of M 1 , the percent being relative to the weight of the polycarbonate.
2. The composition of claim 1 wherein the antimicrobial compound is present in an amount of 0.1 to 3.5 weight percent.
3. The composition of claim 1 wherein the antimicrobial compound is a member selected from the group consisting of Ag 0.005 Li 0.995 Zr 2 (PO 4 ) 3 ; Ag 0.01 (NH 4 ) 0.99 Zr 2 (PO 4 ) 3 ; Ag 0.05 Na 0.95 Zr 2 (PO 4 ) 3 ; Ag 0.2 K 0.8 Ti 2 (PO 4 ) 3 ; Ag 0.05 H 0.05 Na 0.90 Zr 2 (PO 4 ) 3 ; and Ag 0.05 H 0.55 Na 0.40 Zr 2 (PO 4 ) 3 .
4. The composition of claim 1 wherein antimicrobial compound conforms to
Na x H y Ag z Zr 2 (PO 4 ) 3
where x+y+z=1.
5. An article of manufacture comprising the composition of claim 1 .
6. A transparent thermoplastic molding composition comprising aromatic polycarbonate resin and 0.1 to 3.5 weight percent of an antimicrobial compound conforming to formula (I)
Ag a M 1 b M 2 2 (PO 4 ) 3 (I)
wherein M 1 is at least one ion selected from the group consisting of alkali metal ion, alkaline earth metal ion and ammonium ion, M 2 is a tetravalent metal selected from the group consisting of Ti, Zr and Sn, a and b are positive numbers and a+mb=1 where m is a valence of M 1 , the percent being relative to the weight of the polycarbonate, said composition including no benzotriazole.
7. The composition of claim 6 wherein the antimicrobial compound is a member selected from the group consisting of Ag 0.005 Li 0.995 Zr 2 (PO 4 ) 3 ; Ag 0.01 (NH 4 ) 0.99 Zr 2 (PO 4 ) 3 ; Ag 0.05 Na 0.95 Zr 2 (PO 4 ) 3 ; Ag 0.2 K 0.8 Ti 2 (PO 4 ) 3 ; Ag 0.05 H 0.05 Na 0.90 Zr 2 (PO 4 ) 3 ; and Ag 0.05 H 0.55 Na 0.40 Zr 2 (PO 4 ) 3 .
8. The composition of claim 6 wherein antimicrobial compound conforms to
Na x H y Ag z Zr 2 (PO 4 ) 3
where x+y+z=1.
9. An article of manufacture comprising the composition of claim 6 .
10. A thermoplastic molding composition characterized by its high transparency comprising aromatic polycarbonate resin and 0.1 to 3.5 weight percent of an antimicrobial compound conforming to formula (I)
Ag a M 1 b M 2 2 (PO 4 ) 3 (I)
wherein M 1 is at least one ion selected from the group consisting of alkali metal ion, alkaline earth metal ion and ammonium ion, M 2 is a tetravalent metal selected from the group consisting of Ti, Zr and Sn, a and b are positive numbers and a+mb=1 where m is a valence of M 1 , the percent being relative to the weight of the polycarbonate, said composition including no benzotriazole, said transparency determined as at least 211 lines per inch in accordance with ISO 12233 standard on a flat test specimen 0.1″ thick.