Room temperature curable organopolysiloxane composition
View Patent ↗This invention relates to a room temperature curable composition containing, inter alia, diorganopolysiloxane(s) and organic nanoclay(s), the cured composition exhibiting low permeability to gas(es).
1. A curable composition comprising:
a) at least one silanol-terminated diorganopolysiloxane;
b) at least one alkylsilicate crosslinker having the formula:
(R 14 O)(R 15 O)(R 16 O)(R 17 O)Si
where R 14 , R 15 , R 16 and R 17 are chosen independently from monovalent C 1 to C 60 hydrocarbon radicals;
c) at least one catalyst for the crosslinking reaction;
d) at least one orcianic nanoclay; and, optionally; and
e) at least one solid polymer having a permeability to gas that is less than the permeability of the crosslinked diorganopolysiloxane(s).
2. The composition of claim 1 wherein catalyst (c) is a tin catalyst.
3. The composition of claim 2 wherein the tin catalyst is selected from the group consisting of dibutyltindilaurate, dibutyltindiacetate, dibutyltindimethoxide, tinoctoate, isobutyltintriceroate, dibutyltinoxide, dibutyltin bis-diisooctylphthalate, bis-tripropoxysilyl dioctyltin, dibutyltin bis-acetylacetone, silylated dibutyltin dioxide, carbomethoxyphenyl tin tris-uberate, isobutyltin triceroate, dimethyltin dibutyrate, dimethyltin di-neodecanoate, triethyltin tartarate, dibutyltin dibenzoate, tin oleate, tin naphthenate, butyltintri-2-ethylhexylhexoate, tinbutyrate, diorganotin bis β-diketonates and mixtures thereof.
4. The composition of claim 1 wherein the nanoclay portion of organic nanoclay (d) is selected from the group consisting of montmorillonite, sodium montmorillonite, calcium montmorillonite, magnesium montmorillonite, nontronite, beidellite, volkonskoite, laponite, hectorite, saponite, sauconite, magadite, kenyaite, sobockite, svindordite, stevensite, vermiculite, halloysite, aluminate oxides, hydrotalcite, illite, rectorite, tarosovite, ledikite, kaolinite and, mixtures thereof.
5. The composition of claim 1 wherein the organic portion of organic nanoclay (d) is at least one tertiary amine compound R 3 R 4 R 5 N and/or quarternary ammonium compound R 6 R 7 R 8 N + X − wherein R 3 , R 4 , R 5 , R 6 , R 7 and R 8 each independently is an alkyl, alkenyl or alkoxy silane group of up to 60 carbon atoms and X is an anion.
6. The composition of claim 4 wherein the nanoclay portion of organic nanoclay (d) is modified with ammonium, primary alkylammonium, secondary alkylammonium, tertiary alkylammonium quaternary alkylammonium, phosphonium derivatives of aliphatic, aromatic or arylaliphatic amines, phosphines or sulfides or sulfonium derivatives of aliphatic, aromatic or arylaliphatic amines, phosphines or sulfides.
7. The composition of claim 1 wherein solid polymer (e) is selected from the group consisting of low density polyethylene, very low density polyethylene, linear low density polyethylene, high density polyethylene, polypropylene, polyisobutylene, polyvinyl acetate, polyvinyl alcohol, polystyrene, polycarbonate, polyester, such as, polyethylene terephthalate, polybutylene terephthalate, polyethylene napthalate, glycol-modified polyethylene terephthalate, polyvinylchloride, polyvinylidene chloride, polyvinylidene fluoride, thermoplastic polyurethane, acrylonitrile butadiene styrene, polymethylmethacrylate, polyvinyl fluoride, polyamides, polymethylpentene, polyimide, polyetherimide, polether ether ketone, polysulfone , polyether sulfone, ethylene chlorotrifluoroethylene, polytetrafluoroethylene, cellulose acetate, cellulose acetate butyrate, plasticized polyvinyl chloride, ionomers, polyphenylene sulfide, styrene-maleic anhydride, modified polyphenylene oxide, ethylene-propylene rubber, polybutadiene, polychloroprene, polyisoprene, polyurethane, styrene-butadiene-styrene, styrene-ethylene-butadiene-styrene, polymethylphenyl siloxane and mixtures thereof.
8. The composition of claim 1 which further comprises at least one optional component selected from the group consisting of adhesion promoter, surfactant, colorant, pigment, plasticizer, filler other than organic nanoclay, antioxidant, UV stabilizer, and biocide.
9. The composition of claim 8 wherein the adhesion promoter is selected from the group consisting of n-2-aminoethyl-3-aminopropyltrimethoxysilane, 1,3,5-tris(trimethoxysilylpropyl)isocyanurate, γ-aminopropyltriethoxysilane, γ-aminopropyltrimethoxysilane, aminopropyltrimethoxysilane, bis-γ-trimethoxysilypropyl)amine, N-Phenyl-γ-aminopropyltrimethoxysilane, triaminofunctionaltrimethoxysilane, γ-aminopropylmethyldiethoxysilane, γ-aminopropylmethyldiethoxysilane, methacryloxypropyltrimethoxysilane, methylaminopropyltrimethoxysilane, γ-glycidoxypropylethyldimethoxysilane, γ-glycidoxypropyltrimethoxysilane, γ-glycidoxyethyltrimethoxysilane, β-(3,4-epoxycyclohexyl)propyltrimethoxysilane, β(3,4-epoxycyclohexyl) ethylmethyldimethoxysilane, isocyanatopropyltriethoxysilane, isocyanatopropylmethyldimethoxysilane, β-cyanoethyltrimethoxysilane, γ-acryloxypropyltrimethoxysilane, γ-methacryloxypropylmethyldimethoxysilane, 4-amino-3,3,-dimethylbutyltrimethoxysilane, n-ethyl-3-trimethoxysilyl-2-methylpropanamine, and mixtures thereof.
10. The composition of claim 8 wherein the surfactant is a nonionic surfactant selected from the group consisting of polyethylene glycol, polypropylene glycol, ethoxylated castor oil, oleic acid ethoxylate, alkylphenol ethoxylates, copolymers of ethylene oxide and propylene oxide and copolymers of silicones and polyethers, copolymers of silicones and copolymers of ethylene oxide and propylene oxide and mixtures thereof.
11. The composition of claim 10 wherein the non-ionic surfactant is selected from the group consisting of copolymers of ethylene oxide and propylene oxide, copolymers of silicones and polyethers, copolymers of silicones and copolymers of ethylene oxide and propylene oxide and mixtures thereof.
12. The composition of claim 8 wherein the filler other than the organic nanoclay is selected from the group consisting of calcium carbonate, precipitated calcium carbonate, colloidal calcium carbonate, calcium carbonate treated with compounds stearate or stearic acid, fumed silica, precipitated silica, silica gels, hydrophobized silicas, hydrophilic silica gels, crushed quartz, ground quartz, alumina, aluminum hydroxide, titanium hydroxide, clay, kaolin, bentonite montmorillonite, diatomaceous earth, iron oxide, carbon black and graphite, mica, talc, and mixtures thereof.
13. The cured composition of claim 1 .
14. The cured composition of claim 7 .
15. The cured composition of claim 8 .
16. The composition of claim 13 exhibiting an argon permeability coefficient of not greater than about 900 barrers.
17. The composition of claim 14 exhibiting an argon permeability coefficient of not greater than about 900 barrers.
18. The composition of claim 15 exhibiting an argon permeability coefficient of not greater than about 900 barrers.
19. The composition of claim 1 wherein the composition is a curable sealant.
20. The composition of claim 1 wherein the composition is a cured sealant.
21. The composition of claim 13 wherein the composition is a curable sealant.
22. The composition of claim 13 wherein the composition is a cured sealant.
23. The composition of claim 9 wherein the composition is a cured adhesive.
24. The composition of claim 13 wherein the composition is a curable adhesive.
25. The composition of claim 13 wherein the composition is a cured adhesive.