Method for wrapping a non-porous substrate object with a wood veneer
There is described a method for at least partially covering selected surfaces of a non-porous substrate with a flexible veneer, the method comprising the steps of maintaining a humid environment during the covering of said substrate with the veneer, applying a preheated adhesive to one or both of the substrate and the veneer, progressively shaping the veneer to the selected surfaces of the substrate through the application of pressure biasing the veneer against the selected surfaces and curing the assembly of the veneer and the substrate.
1. A method for at least partially covering selected surfaces of a non-porous substrate with a flexible wood veneer, the method comprising the steps of:
maintaining a humid environment, a relative humidity is maintained at approximately 40% for ambient temperatures in a selected temperature range during the covering of said substrate with said veneer so that the veneer in the environment is exposed to the humidity for flexibility of the veneer;
applying an adhesive to one or both of said substrate and said veneer, said adhesive being preheated to a temperature selected on the basis of the temperature and the relative humidity in the environment;
progressively shaping said veneer to said selected surfaces of said substrate through the application of pressure biasing said veneer against said selected surfaces; and
curing the assembly of said veneer and said substrate.
2. The method of claim 1 wherein said adhesive is preheated to a temperature in the range of about 110° to about 130° Celsius.
3. The method of claim 1 wherein said pressure biasing said veneer against said substrate is applied by a plurality of pressure application means.
4. The method of claim 3 wherein said pressure application means comprise rollers arranged to sequentially bias said veneer against said selected surfaces of said substrate to complete the covering thereof.
5. The method of claim 4 wherein said veneer and said substrate are moved continuously past said rollers for the covering of a predetermined length of said substrate.
6. The method of claim 2 , wherein said substrate is preheated to be at a temperature in the range of about 30° to 40° Celsius prior to being covered by the veneer.
7. The method of claim 6 wherein the step of maintaining a humid environment includes wetting an outer surface of said veneer with a mist of water.
8. The method of claim 2 wherein said adhesive is a fast hardening, permanent adhesive.
9. The method of claim 8 wherein said adhesive is a polyurethane reactive adhesive.
10. The method of claim 1 wherein said curing is at least partially performed by means of microwave flash-off.
11. The method of claim 10 wherein said curing is by means of ultraviolet curing.
12. The method of claim 1 wherein said humid environment is maintained for an ambient temperature of about 20° Centigrade.
13. The method of claim 1 wherein said substrate is an aluminum extrusion.
14. The method of claim 13 wherein said veneer is a raw wood veneer without a backing material on a surface of said veneer that is adhered to said substrate.
15. A method for at least partially covering selected surfaces of a non-porous substrate with a flexible wood veneer, the method comprising the steps of:
maintaining a humid environment at about 40% relative humidity for a temperature of about 20° Centigrade by wetting an outer surface of said veneer with a mist of water during the covering of said substrate with said veneer so that the veneer in the environment is exposed to the humidity for flexibility of the veneer;
applying an adhesive to one or both of said substrate and said veneer, said adhesive being preheated to a temperature selected on the basis of the temperature and the relative humidity in the environment;
progressively shaping said veneer to said selected surfaces of said substrate through the application of pressure biasing said veneer against said selected surfaces; and
curing the assembly of said veneer and said substrate.
16. The method of claim 15 wherein said adhesive is preheated to a temperature in the range of about 110° to about 130° Celsius.
17. The method of claim 15 wherein said veneer or selected portions thereof are reduced in thickness to facilitate the shaping thereof about said substrate.
18. The method of claim 15 wherein said pressure biasing said veneer against said substrate is applied by a plurality of pressure application means.
19. The method of claim 18 wherein said pressure application means comprise rollers arranged to sequentially bias said veneer against said selected surfaces of said substrate to complete the covering thereof.
20. The method of claim 16 , wherein said substrate is preheated to be at a temperature in the range of about 30° to 40° Celsius prior to being covered by the veneer.
21. The method of claim 16 wherein said adhesive is a fast hardening, permanent adhesive.
22. The method of claim 21 wherein said adhesive is a polyurethane reactive adhesive.
23. The method of claim 15 wherein said curing is at least partially performed by means of microwave flash-off.
24. The method of claim 23 wherein said curing is by means of ultraviolet curing.
25. The method of claim 1 wherein said substrate is an aluminum extrusion.
26. The method of claim 25 wherein said is a raw wood veneer without a backing material on a surface of said veneer that is adhered to said substrate.
27. A method for at least partially covering selected surfaces of a non-porous substrate with a flexible wood veneer, the method comprising the steps of:
maintaining a humid environment at about 40% relative humidity within a selected relative humidity range and a selected temperature range during the covering of said substrate with said veneer so that the veneer in the environment absorbs at least some of the humidity for flexibility of the veneer;
applying an adhesive to one or both of said substrate and said veneer, said adhesive being preheated to a temperature selected on the basis of the temperature and the relative humidity in the environment;
progressively shaping said veneer to said selected surfaces of said substrate through the application of pressure biasing said veneer against said selected surfaces; and
curing the assembly of said veneer and said substrate.
28. The method of claim 27 , wherein said adhesive is preheated to a temperature in the range of about 110° to about 130° Celsius.
29. The method of claim 28 , wherein said substrate is preheated to a temperature in the range of about 30° to 40° Celsius prior to being covered by the veneer.