Extrusion coating process and coated substrates having improved heat seal properties
An extrusion coating process for the production of extrusion coated substrates having improved heat seal properties at temperatures within the low heat seal range is provided. The process utilizes a combination of ethylene-vinyl acetate copolymers having different vinyl acetate contents.
1 . In a process for the production of heat sealable extrusion coated substrates having improved heat seal properties, the process comprising:
(a) providing a first EVA copolymer having a VA content from 9 to 20 wt. % and MI from 7 to 35 g/10 min;
(b) providing a second EVA copolymer having a VA content from 22 to 34 wt. % and MI from 7 to 35 g/10 min;
(c) combining said first and second EVA copolymers at a wt. ratio of 3:1 to 1:3 to produce a mixture having a VA content from 15 to 28 wt. % and MI from 15 to 35 g/10 min;
(d) melt blending the mixture obtained from step (c); and
(e) extrusion coating at least one side of a substrate with the melt blended product produced in step (d).
2 . The process of claim 1 wherein the first EVA copolymer has a VA content from 12 to 20 wt. %.
3 . The process of claim 1 wherein the second EVA copolymer has a VA content from 24 to 32 wt. %.
4 . The process of claim 1 wherein the first and second EVA copolymers are combined at a weight ratio of 2.5:1 to 1:2.5.
5 . The process of claim 4 wherein the mixture of first and second EVA copolymers has a VA content from 17 to 26 wt. % and MI from 17 to 32 g/10 min.
6 . An extrusion coated substrate produced by the process of claim 1 and further characterized by having improved heat seal properties in the low heat seal temperature range.
7 . The extrusion coated substrate of claim 6 wherein the extrusion coating is applied to a thickness of 0.2 to 1.5 mils and the substrate is selected from the group consisting of fabrics, paper products, plastic materials and metal foils.
8 . The extrusion coated substrate of claim 7 wherein the extrusion coating is a blend of first and second EVA copolymers having an MI from 17 to 32 g/10 min and weight average VA content from 17 to 26 wt. %.
9 . The extrusion coated substrate of claim 8 wherein the first EVA copolymer has a VA content from 12 to 20 wt. % and the second EVA copolymer has a VA content from 24 to 32 wt. %.
10 . The extrusion coated substrate of claim 8 wherein the first and second EVA copolymers are combined at a weight ratio of 2.5:1 to 1:2.5.